TIDMCCZ
RNS Number : 2178R
Castillo Copper Limited
28 February 2023
28 February 2023
CASTILLO COPPER LIMITED
("Castillo", or the "Company")
Encouraging REE metallurgy test-work from Broken Hill
Castillo Copper Limited (LSE and ASX: CCZ), a base metal
explorer primarily focused on copper across Australia and Zambia,
is pleased to announce encouraging results from initial Rare Earth
Element ("REE") metallurgical test-work at the Fence Gossan
Prospect (Appendix A) within the BHA Project's East Zone.
HIGHLIGHTS:
-- Preliminary metallurgical test-work on a 20m composite sample
from the Fence Gossan Prospect (FG_003RC) delivered encouraging
results, with clays - subjected to froth flotation - obtaining up
to 2-3 times REE enrichment from the head grade at up to 70%
recovery (refer Figure 1 and Appendix B for full details) :
o These findings confirm REEs can be readily separated from clay
within the East Zone discovery area and potentially beneficiated to
a higher grade concentrate
-- To acquire a deeper understanding of the potential to extract
REE-mineralisation from clays in the East Zone discovery area, the
Board has approved appointing a specialist consultancy to conduct
an in-depth metallurgy test-work programme:
o Once completed and interpreted, the results from this
programme will be key to securing interest from potential off-take
partners and providing a path to market
-- Further, 1m re-assays for Reefs Tank were received for all
four drill-holes (RT_001-4RC), which further verified there is an
extensive, shallow REE system apparent across the central part of
the East Zone - the best intercept comprised:
o 3m @ 2,587ppm TREO from 14m (RT_001RC)
-- Reconciling all assays from the recent drilling and auger
campaigns across the Fence Gossan, Tors and Reefs Tanks Prospects,
the geology team has created heat maps which identify zones of high
Total and Magnetic Rare Earth Oxides ("TREO"/"MREO"):
o These areas will be subject to further surface sampling and
geophysical surveys then potentially drill-testing to extend known
mineralisation
Ged Hall, Chairman of Castillo Copper, said : "On a holistic
basis, the Board is delighted with results from the drilling,
surface sampling and metallurgical test-work at Broken Hill as they
collectively demonstrate the forward value creating potential of
the BHA Project's East Zone. In short, the underlying REE system is
shallow, extends over at least 4.5km(2) , delivered results up to
3,491ppm TREO and produced up to 38.9% MREO in diamond core(1) .
Moreover, the metallurgy test-work proves REE mineralisation
readily separates from clay and can potentially be beneficiated to
a higher-grade concentrate. By all accounts, this is an excellent
report card ahead of exploratory work ramping up."
ENCOURAGING METALLURGICAL TEST-WORK RESULTS
FIGURE A1: HEAD ASSAY / IMPROVEMENT
ANALYTE ALS Adelaide ALS Perth Times
Improvement
REE ME-MS81 HEAD
GRADE
REE COMP
%
%
============== ===========
Ce (%) 0.045 0.05 1.6
============== =========== =============
La (%) 0.038 0.03 2.3
============== =========== =============
Nd (%) 0.021 0.02 2.0
============== =========== =============
Pr (%) 0.006 0.01 1.3
============== =========== =============
Y (%) 0.009 0.01 1.1
============== =========== =============
Source: ALS
To follow up on these excellent results, the Board has now
approved the appointment of a specialist metallurgy consultancy
with extensive experience in how REE mineralisation liberates from
various host rocks (including clays). The Board wants a deeper
understanding of the potential to extract REE mineralisation from
the East Zone discovery area, as this information will be key to
securing interest from potential off-take partners that can provide
a clear path to market.
Reefs Tank Assays
All 1m re-assays for Reefs Tank were received for the four
drill-holes (RT_001-4RC), with up to 2,587ppm TREO recorded (Figure
1). On a holistic basis, the Reefs Tank results provide incremental
evidence there is an extensive, shallow REE system apparent across
the central part of the BHA Project's East Zone (Appendix A).
FIGURE 1 : REEFS TANK 1M ASSAYS
Hole From To Width Ag Th U TREO TREO-Ce LREO HREO CREO MREO
(m) (m) (m) (g/t) (ppm) (ppm) (ppm) (ppm) (ppm) (ppm) (%) (%)
===== ===== ====== ======= ======= ======= ======= ======== ======== ======== ======
RT_001RC 11 13 2 0.05 17.0 5.4 631 313.08 490.55 140.69 27.3% 20.6%
===== ===== ====== ======= ======= ======= ======= ======== ======== ======== ====== ======
RT_001RC 14 17 3 0.96 29.9 9.4 2,587 2187.30 1105.24 1481.70 55.7% 24.7%
===== ===== ====== ======= ======= ======= ======= ======== ======== ======== ====== ======
RT_001RC 54 55 1 0.15 70.2 9.2 796 429.43 746.15 49.34 20.8% 29.1%
===== ===== ====== ======= ======= ======= ======= ======== ======== ======== ====== ======
RT_001RC 55 56 1 0.08 80.5 6.2 896 487.84 838.19 57.49 21.2% 29.9%
===== ===== ====== ======= ======= ======= ======= ======== ======== ======== ====== ======
RT_001RC 64 65 1 0.12 121.0 9.0 1,236 658.75 1196.01 40.09 19.0% 29.3%
===== ===== ====== ======= ======= ======= ======= ======== ======== ======== ====== ======
RT_002RC 0 1 1 0.06 19.8 2.5 367 241.55 272.76 94.70 34.1% 28.2%
===== ===== ====== ======= ======= ======= ======= ======== ======== ======== ====== ======
RT_002RC 1 4 3 0.11 24.7 2.5 449 285.00 350.63 98.36 31.5% 27.6%
===== ===== ====== ======= ======= ======= ======= ======== ======== ======== ====== ======
RT_002RC 28 32 4 0.12 54.6 3.5 601 343.27 541.76 59.48 24.1% 30.9%
===== ===== ====== ======= ======= ======= ======= ======== ======== ======== ====== ======
RT_002RC 64 68 4 0.05 27.6 3.2 430 267.15 339.41 90.36 30.7% 27.5%
===== ===== ====== ======= ======= ======= ======= ======== ======== ======== ====== ======
RT_003RC 0 4 4 nd 14.6 6.2 247 165.15 183.62 63.40 34.5% 29.8%
===== ===== ====== ======= ======= ======= ======= ======== ======== ======== ====== ======
RT_003RC 8 16 8 nd 27.5 4.5 424 258.35 352.12 71.76 28.4% 28.5%
===== ===== ====== ======= ======= ======= ======= ======== ======== ======== ====== ======
RT_003RC 56 64 8 nd 23.8 3.8 389 237.70 313.43 75.97 29.6% 27.6%
===== ===== ====== ======= ======= ======= ======= ======== ======== ======== ====== ======
RT_003RC 72 76 4 nd 28.6 6.9 450 272.82 366.14 83.72 29.1% 27.3%
===== ===== ====== ======= ======= ======= ======= ======== ======== ======== ====== ======
RT_004RC 52 56 4 0.25 44.4 4.1 567 344.40 465.92 101.13 29.1% 29.2%
===== ===== ====== ======= ======= ======= ======= ======== ======== ======== ====== ======
RT_004RC 84 92 8 1.78 25.6 8.5 525 314.92 433.13 92.23 28.4% 27.7%
===== ===== ====== ======= ======= ======= ======= ======== ======== ======== ====== ======
Source: CCZ geology team
TREO / MREO Contours
After reconciling all assays from the recent drilling and auger
campaigns across the Fence Gossan, Tors & Reefs Tanks Prospects
(Appendix B), the geology team has created heat maps which identify
zones of high TREO and MREO (Figure 2 & 3).
These areas will be subject to further surface sampling and
geophysical campaigns (including trial transects of ground
radiometric and EM surveys) then potentially drill-testing (red
zones in Figure 2) to extend known mineralisation.
Note, the TREO is the sum of REEs in ppm, calculated from
ME-MS81 method, converted to their stoichiometric equivalent i.e.,
Ce converted to CeO(2) and so forth. The high-value Magnetic REO
comprise Nd+Pr+Dy+Tb and generally command premium pricing to other
REEs as they are in strong demand. Refer to Appendix C for a full
explanation and TREO calculation.
FIGURE 2: FENCE GOSSAN AND SURROUNDS SURFACE SAMPLING - TREO IN
PPM
Source: CCZ geology team
FIGURE 3: FENCE GOSSAN AND SURROUNDS SURFACE SAMPLING - MREO
ppm
Notes: All coordinates in MGA94-Z54S Source: CCZ Geology
team
For further information, please contact:
Castillo Copper Limited +61 8 6558 0886
Dr Dennis Jensen (Australia), Managing Director
Gerrard Hall (UK), Chairman
SI Capital Limited (Financial Adviser and Corporate Broker) +44 (0)1483 413500
Nick Emerson
Gracechurch Group (Financial PR) +44 (0)20 4582 3500
Harry Chathli, Alexis Gore, Henry Gamble
About Castillo Copper
Castillo Copper Limited is an Australian-based explorer
primarily focused on copper across Australia and Zambia. The group
is embarking on a strategic transformation to morph into a mid-tier
copper group underpinned by its core projects:
-- A large footprint in the Mt Isa copper-belt district,
north-west Queensland, which delivers significant exploration
upside through having several high-grade targets and a sizeable
untested anomaly within its boundaries in a copper-rich region.
-- Four high-quality prospective assets across Zambia's
copper-belt which is the second largest copper producer in
Africa.
-- A large tenure footprint proximal to Broken Hill's
world-class deposit that is prospective for
zinc-silver-lead-copper-gold and platinoids.
-- Cangai Copper Mine in northern New South Wales, which is one
of Australia's highest grading historic copper mines.
The group is listed on the LSE and ASX under the ticker
"CCZ."
Competent Person's Statement
The information in this report that relates to Exploration
Results and Mineral Resource Estimates for "BHA Project, East Zone"
is based on information compiled or reviewed by Mr Mark Biggs. Mr
Biggs is a director of ROM Resources, a company which is a
shareholder of Castillo Copper Limited. ROM Resources provides ad
hoc geological consultancy services to Castillo Copper Limited. Mr
Biggs is a member of the Australian Institute of Mining and
Metallurgy (member #107188) and has sufficient experience of
relevance to the styles of mineralisation and types of deposits
under consideration, and to the activities undertaken, to qualify
as a Competent Person as defined in the 2012 Edition of the Joint
Ore Reserves Committee (JORC) Australasian Code for Reporting of
Exploration Results, and Mineral Resources. Mr Biggs holds an
AusIMM Online Course Certificate in 2012 JORC Code Reporting. Mr
Biggs also consents to the inclusion in this report of the matters
based on information in the form and context in which it
appears.
References
1) CCZ ASX Release - 15 February 2023
APPIX A: BHA PROJECT'S EAST ZONE
FIGURE A1: BHA PROJECT's EAST ZONE - REE EXPLORATION
FOOTPRINT
Source: CCZ geology team
FIGURE A2: BHA PROJECT
Source: CCZ geology team
APPIX B: PRELIMINARY METALLURGY TESTWORK
Background and Scope
A composite sample of RC chips from Fence Gossan drill-hole
FG_003RC was constructed over the interval from 0-20m. The material
reported over that interval had lithology logged as clay,
haematite, goethite, and extremely weathered pegmatite. The main
rare-containing minerals are thought to be monazite, allanite,
xenotime, and possibly baryte or celsian (to account for the high
barium contents of some samples). Note, these assumptions need to
be tested by XRD and/or QEM-SEM testing.
The composite was made up of 1m samples tested using ME-MS81
analysis method (the results for which are provided in Figure
A1).
The process methodology followed by ALS Perth was as
follows:
-- Rotary Blending & Splitting (12x1kg, reserve)
-- PPS - Head Assay Submission
-- Assay - Head Assay (Ce, La, Nd, Pr, SiO(2) , Y)
-- 1kg Grind Establishment (P80 53<MU>m assumed)
-- Rougher Flotation (6 con, 1 Tail)
-- PPS - Float Products
-- Assay - Head Assay (Ce, La, Nd, Pr, SiO(2) , and Y)
Results
The head grade and froth flotation improvement are shown in
Figure A1.
FIGURE A1: HEAD ASSAY / IMPROVEMENT
ANALYTE ALS Adelaide ALS Perth Times
Improvement
REE ME-MS81 HEAD
GRADE
REE COMP
%
%
Ce (%) 0.045 0.05 1.6
============== =========== =============
La (%) 0.038 0.03 2.3
============== =========== =============
Nd (%) 0.021 0.02 2.0
============== =========== =============
Pr (%) 0.006 0.01 1.3
============== =========== =============
SiO2 NT 64.3 -
(%)
============== =========== =============
Y (%) 0.009 0.01 1.1
============== =========== =============
Source: ALS
Overall main laboratory observations of note are:
-- Slurry was highly viscous after ALS Perth added lime that
changed the target pH down to 9.5. The process was changed to soda
ash in the second test.
-- By end of float, ALS Perth saw froth instability, which
indicates what material wanted to float.
-- There was a colour trend in the concentrate progressing through the stages.
Figures A2 to A5 show cumulative recovery versus grade for the
Ce, La, Nd, and Pr components.
FIGURE A1: CERIUM CUMULATIVE GRADE / RECOVERY
Source: ALS
FIGURE A1: LANTHANUM CUMULATIVE GRADE / RECOVERY
Source: ALS
FIGURE A1: NEODYMIUM UMULATIVE GRADE / RECOVERY
Source: ALS
FIGURE A5: PRASEODYMIUM CUMULATIVE GRADE / RECOVERY
Source: ALS
FIGURE A6: FLOWTATION FLOWSHEET
Source: ALS
FIGURE A7: DRILLHOLE FG_003RC - 0 TO 20M COMPOSITE USED FOR ALS
PERTH METALLURGICAL TESTING, 1M ANALYSIS (A-P)
Sample From Length PGM-MS23 PGM-MS23 PGM-MS23 ME-MS81 ME-MS81 ME-MS81 ME-MS81 ME-MS81 ME-MS81 ME-MS81 ME-MS81 ME-MS81 ME-MS81 ME-MS81 ME-MS81 ME-MS81 ME-MS81 ME-MS81 ME-MS81
Number To
Au Pt Pd Ba Ce Cr Cs Dy Er Eu Ga Gd Hf Ho La Lu Nb Nd Pr
===== === ======= ========= ========= ========= ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ========
m m m ppm ppm ppm ppm ppm ppm ppm ppm ppm ppm ppm ppm ppm ppm ppm ppm ppm ppm ppm
===== === ======= ========= ========= ========= ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ========
CCZ04511 0 1 1 0.002 0.001 0.002 297 131 61 3.13 6.48 3.92 1.71 23.5 7.17 5.56 1.35 70 0.58 10.85 54.8 16.1
===== === ======= ========= ========= ========= ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ========
CCZ04512 1 2 1 0.006 0.0013 0.003 910 172.5 73 2.58 7.57 4.05 2.16 38.1 8.71 4.09 1.52 97.5 0.46 10.55 74.2 21
===== === ======= ========= ========= ========= ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ========
CCZ04513 2 3 1 0.004 0.0011 0.002 648 696 71 2.64 20.9 9.3 9.12 46.2 34.4 4.18 3.6 409 0.93 12.75 347 94.2
===== === ======= ========= ========= ========= ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ========
CCZ04514 3 4 1 0.002 0.0007 0.001 166.5 580 72 5.2 17.85 6.75 7.5 55.9 28.5 3.02 2.76 369 0.54 10.4 276 74.4
===== === ======= ========= ========= ========= ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ========
CCZ04515 4 5 1 0.002 0.0007 0.001 143 511 80 5.01 16.35 6.43 6.46 51.2 25.9 3.39 2.67 336 0.63 13.85 252 67.4
===== === ======= ========= ========= ========= ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ========
CCZ04516 5 6 1 0.001 0.0008 0.001 98.4 376 75 3.04 10.5 3.86 3.91 53.5 17.5 3.05 1.62 229 0.36 12.8 175.5 46.6
===== === ======= ========= ========= ========= ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ========
CCZ04517 6 7 1 <0.001 0.0008 0.001 91.9 480 76 3.89 13.75 4.51 5.55 54.5 22.4 3.37 2.03 293 0.47 11.9 221 59.8
===== === ======= ========= ========= ========= ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ========
CCZ04518 7 8 1 <0.001 0.0007 0.001 59.1 332 90 3.2 8.64 3.14 3.43 60.5 14.3 3.18 1.33 204 0.28 15.4 142.5 39.3
===== === ======= ========= ========= ========= ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ========
CCZ04519 8 9 1 <0.001 0.0007 0.001 87.2 422 88 5.13 12.5 5.17 4.67 53.4 19 2.97 2.05 258 0.6 12.55 184.5 49.7
===== === ======= ========= ========= ========= ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ========
CCZ04520 9 10 1 <0.001 0.0008 0.001 94.5 287 78 5.62 7.68 3.76 2.49 56.5 10.55 2.62 1.37 175 0.49 13.2 116.5 31.3
===== === ======= ========= ========= ========= ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ========
CCZ04521 10 11 1 0.001 0.0007 0.001 110.5 366 81 6.57 8.9 4.09 3.31 48.3 14.05 2.56 1.69 231 0.55 10.95 145.5 42.6
===== === ======= ========= ========= ========= ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ========
CCZ04522 11 12 1 <0.001 0.0007 0.001 118.5 384 90 6.47 12.3 6.33 3.66 58.3 16.7 2.95 2.2 258 0.92 13.1 158.5 43.4
===== === ======= ========= ========= ========= ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ========
CCZ04523 12 13 1 <0.001 0.0007 0.001 88.6 292 85 3.63 9.33 5.15 2.71 57.2 12.45 3.51 1.79 202 0.61 12.7 117 32.1
===== === ======= ========= ========= ========= ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ========
CCZ04524 13 14 1 <0.001 0.0007 0.001 98.8 318 81 5.38 12.6 5.77 4.14 56.9 17.65 2.9 2.28 233 0.68 13.15 145.5 38.3
===== === ======= ========= ========= ========= ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ========
CCZ04525 14 15 1 <0.001 0.0009 0.001 45.7 486 91 4.58 17.9 6.78 5.7 63 28.4 3.06 2.93 341 0.61 12.45 222 59.1
===== === ======= ========= ========= ========= ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ========
CCZ04526 15 16 1 <0.001 0.0008 0.001 69.4 577 71 9.24 29 13.5 7.19 61.2 38.1 3.58 5.31 427 1.5 11.4 266 68.9
===== === ======= ========= ========= ========= ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ========
CCZ04527 16 17 1 0.001 0.0025 0.002 53.4 453 67 5.76 23.3 11.35 5.34 47.1 28 4.04 4.32 322 1.29 10.1 195 50.9
===== === ======= ========= ========= ========= ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ========
CCZ04528 17 18 1 0.003 0.0017 0.002 118 698 53 17.75 30.3 14.65 7.91 48.2 40.5 1.46 5.72 466 1.5 5.57 303 81.5
===== === ======= ========= ========= ========= ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ========
CCZ04529 18 19 1 0.045 0.002 0.002 109 774 54 6.11 42.4 16.05 12.35 40.3 60.8 1.61 6.9 644 1.36 6.51 425 106.5
===== === ======= ========= ========= ========= ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ========
CCZ04530 19 20 1 0.005 0.0011 0.001 193 661 60 2.69 104.5 69.3 15.6 25.8 100 2.98 23.8 597 8.34 7 403 94.2
===== === ======= ========= ========= ========= ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ========
Average 180.0 449.8 74.9 5.4 20.6 10.2 5.7 50.0 27.3 3.2 3.9 308.1 1.1 11.4 211.2 55.9
===== === ======= ========= ========= ========= ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ========
Source: ALS Adelaide methods ME-MS81 and PGM-MS23 used.
Drillhole FG_003RC drilled October 2022.
FIGURE A7: DRILLHOLE FG_003RC - 0 TO 20M COMPOSITE USED FOR ALS
PERTH METALLURGICAL TESTING, 1M ANALYSIS (CONT)
Sample From Length ME-MS81 ME-MS81 ME-MS81 ME-MS81 ME-MS81 ME-MS81 ME-MS81 ME-MS81 ME-MS81 ME-MS81 ME-MS81 ME-MS81 ME-MS81 ME-MS81 ME-MS81 ME-MS81
Number To
Rb Sc Sm Sn Sr Ta Tb Th Ti Tm U V W Y Yb Zr
===== === ======= ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ========
m m m ppm ppm ppm ppm ppm ppm ppm ppm % ppm ppm ppm ppm ppm ppm ppm
===== === ======= ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ========
CCZ04511 0 1 1 67.5 16.4 10.3 3.2 128 0.9 1.18 12.85 0.49 0.59 4.02 190 3.1 37 3.69 223
===== === ======= ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ========
CCZ04512 1 2 1 51.2 20 12.35 2.4 180 0.8 1.28 13.65 0.41 0.55 7.54 247 4 35.3 3.39 134
===== === ======= ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ========
CCZ04513 2 3 1 51.7 19.4 52.8 3.2 126 1 4.53 14.55 0.38 1.18 15.65 191 4.4 76.9 7.01 137
===== === ======= ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ========
CCZ04514 3 4 1 92.2 37.5 41.8 3.5 129.5 1 3.79 16.3 0.33 0.84 13.85 171 2.8 50.3 5.02 109
===== === ======= ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ========
CCZ04515 4 5 1 89.1 27.5 38.7 4.3 109.5 1.2 3.52 14.95 0.4 0.78 12.5 178 2.8 53.6 5.09 110
===== === ======= ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ========
CCZ04516 5 6 1 51.2 14.7 25.9 3.5 91.3 1.1 2.28 16.25 0.38 0.55 7.46 129 3.7 30.9 2.88 100
===== === ======= ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ========
CCZ04517 6 7 1 78.9 14.7 33.2 2.6 99.1 1 2.98 16.35 0.34 0.57 9.41 106 4.3 35.8 3.23 110
===== === ======= ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ========
CCZ04518 7 8 1 79.8 11.6 22.6 3.2 101 1.2 1.88 18.25 0.38 0.38 7.65 102 6.3 25.5 2.31 107
===== === ======= ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ========
CCZ04519 8 9 1 121 16.7 29 3.6 100 1.2 2.58 14.9 0.35 0.71 10.7 140 3 43.1 4.57 99
===== === ======= ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ========
CCZ04520 9 10 1 160.5 19.6 16.3 3.5 84.7 1.1 1.5 14.3 0.32 0.55 8.74 150 2.2 28.2 4.08 87
===== === ======= ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ========
CCZ04521 10 11 1 196 20.4 21.6 4.1 89.8 0.9 1.96 14.5 0.31 0.59 12.1 149 1.7 33.6 3.97 87
===== === ======= ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ========
CCZ04522 11 12 1 171.5 20.2 24 3.7 117 1.1 2.28 19.6 0.34 0.96 15.85 149 3.5 50.9 6.62 99
===== === ======= ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ========
CCZ04523 12 13 1 108.5 21.4 16.55 3.1 98.9 1.1 1.79 17.65 0.34 0.73 11.2 101 6.3 38.4 4.72 116
===== === ======= ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ========
CCZ04524 13 14 1 131 20.4 22.3 5 103.5 1 2.28 17.3 0.33 0.79 12.5 136 4 49 4.78 97
===== === ======= ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ========
CCZ04525 14 15 1 98.8 15.7 35.2 4.3 88.2 1.1 3.64 18.45 0.36 0.81 14.2 170 3.5 57 5 95
===== === ======= ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ========
CCZ04526 15 16 1 143.5 19.2 41.5 4.3 81.2 1 5.56 18.25 0.31 1.78 20.7 184 2.7 115.5 11.75 113
===== === ======= ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ========
CCZ04527 16 17 1 84.4 17.6 30.9 3.5 64.9 0.9 4.24 12.7 0.27 1.54 19.1 147 3.6 95.8 9.92 142
===== === ======= ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ========
CCZ04528 17 18 1 139.5 17.8 47 3.8 51.4 0.4 5.61 6.91 0.15 1.98 38.1 498 4.2 137 12.55 53
===== === ======= ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ========
CCZ04529 18 19 1 52 38.5 66 5.7 110 0.4 8.47 4.76 0.74 1.94 73.4 580 3 128 11.6 50
===== === ======= ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ========
CCZ04530 19 20 1 32.7 41.9 72.2 1.5 146 0.4 16 1.57 1.11 9.13 48.7 442 1.1 722 57.8 94
===== === ======= ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ========
Average 100.1 21.6 33.0 3.6 105.0 0.9 3.9 14.2 0.4 1.3 18.2 208.0 3.5 92.2 8.5 108.1
===== === ======= ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ======== ========
Source: ALS Adelaide methods ME-MS81 and PGM-MS23 used.
Drillhole FG_003RC drilled October 2022.
APPIX C: REE RESULTS / TREO CONVERSION FACTOR
FIGURE B1: FENCE GOSSAN SURFACE SAMPLING - ALS METHOD ME-MS81
LABORATORY RESULTS
HoleID Sampid Easting Northing from to thickness Th U Ce La Y Dy Er Eu Gd Ho Lu Nd Pr Sm Tb Tm Yb TREO TREO-Ce LREO HREO CREO MREO MREO_%
(ppm) (ppm) (ppm) (ppm) % %
FG_SM_T12 CCZ05627 574597.0 6454393.0 0 0.3 0.3 16.0 2.5 113.5 53.6 41.3 7.49 4.33 1.6 8.57 1.49 0.54 49.3 12.95 9.54 1.31 0.59 4.04 373.4 233.9 286.5 86.9 0.33 0.28 27.9
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_T13 CCZ05628 574601.0 6454194.0 0 0.3 0.3 12.9 2.1 77.7 37.2 36.6 5.95 3.91 1.33 6.33 1.36 0.54 34.9 8.87 6.74 1.03 0.58 3.7 273.2 177.7 198.3 74.9 0.35 0.27 27.3
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_T14 CCZ05629 574600.0 6453990.0 0 0.3 0.3 14.9 2.2 88.6 43.1 31.1 5.25 3.28 1.11 6.03 1.12 0.46 37.7 10.15 7.22 0.95 0.46 3.05 288.4 179.6 224.0 64.4 0.32 0.27 27.3
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_T15 CCZ05630 574600.0 6453791.0 0 0.3 0.3 12.8 1.8 73.9 36.2 30.4 5.16 3.17 1.21 6.01 1.09 0.4 33.4 8.87 6.81 0.91 0.48 3.01 254.0 163.3 190.8 63.2 0.34 0.28 28.1
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_T16 CCZ05631 574599.0 6453588.0 0 0.3 0.3 13.8 1.9 83.5 39.9 32.1 5.65 3.17 1.31 6.31 1.2 0.41 37.7 9.93 7.66 0.99 0.45 2.94 280.8 178.2 214.2 66.5 0.33 0.28 28.4
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_T17 CCZ05632 574602.0 6453389.0 0 0.3 0.3 14.4 2.0 85.2 41.1 33.3 5.52 3.58 1.19 6.08 1.19 0.55 37.4 9.9 6.89 0.92 0.55 3.7 285.5 180.8 216.4 69.0 0.33 0.27 27.3
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_T18 CCZ05633 574598.0 6453194.0 0 0.3 0.3 12.1 1.8 84.4 35.7 29 4.93 3.07 1.22 5.79 1.09 0.41 32.2 8.45 6.07 0.92 0.46 2.89 261.0 157.4 200.4 60.7 0.32 0.26 26.1
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_T19 CCZ05634 574601.0 6452990.0 0 0.3 0.3 13.7 1.9 84.5 41.5 34.6 5.92 3.95 1.34 6.61 1.24 0.48 38.1 9.89 7.45 1.01 0.55 3.64 289.8 186.0 217.5 72.3 0.34 0.28 27.8
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_T20 CCZ05635 574600.0 6452790.0 0 0.3 0.3 18.3 2.6 104.5 51.5 36.1 6.3 3.94 1.32 7.3 1.31 0.46 46.2 12 9.12 1.06 0.53 3.63 343.3 214.9 267.7 75.5 0.32 0.28 27.9
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_U12 CCZ05636 574800.0 6454396.0 0 0.3 0.3 17.9 2.4 108.5 51.6 37.6 6.73 3.74 1.49 7.61 1.33 0.51 46.7 12.8 9.28 1.15 0.58 3.54 352.9 219.6 274.5 78.4 0.32 0.28 27.9
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_U13 CCZ05637 574799.0 6454196.0 0 0.3 0.3 16.6 2.3 98.9 48.7 49.7 8.11 5.28 1.5 9.26 1.82 0.75 46.1 11.95 9.47 1.45 0.8 5.15 360.1 238.6 257.8 102.3 0.36 0.28 28.0
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_U14 CCZ05638 574802.0 6453995.0 0 0.3 0.3 12.5 2.0 75.1 37.5 42.2 6.24 4.31 1.12 6.31 1.49 0.59 33.9 8.91 6.78 0.99 0.71 4.43 278.0 185.8 194.4 83.6 0.37 0.27 26.5
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_U15 CCZ05639 574800.0 6453795.0 0 0.3 0.3 14.8 2.3 79.5 37.4 42 6.89 4.58 1.24 6.76 1.57 0.61 35.5 9.28 7.26 1.15 0.71 4.48 288.0 190.4 202.6 85.5 0.37 0.27 27.1
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_U16 CCZ05640 574803.0 6453599.0 0 0.3 0.3 14.5 2.1 84.8 42.7 37.9 6.2 3.87 1.33 6.34 1.3 0.56 37.9 10.05 7.54 1.06 0.58 3.72 296.1 192.0 219.3 76.8 0.35 0.27 27.3
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_U17 CCZ05641 574800.0 6453399.0 0 0.3 0.3 14.5 2.2 88.7 44.5 32.5 5.49 3.37 1.23 6.04 1.17 0.49 38.8 10.6 7.47 0.98 0.52 3.1 294.9 185.9 227.9 67.0 0.32 0.28 27.5
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_U18 CCZ05642 574800.0 6453199.0 0 0.3 0.3 13.4 2.1 78.3 38.8 32.3 5.35 3.28 1.2 5.69 1.09 0.46 35.1 9.27 7.11 0.86 0.45 3.09 267.7 171.6 202.1 65.7 0.34 0.28 27.7
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_U19 CCZ05643 574799.0 6453000.0 0 0.3 0.3 17.1 2.3 104.5 51 38.2 6.25 3.78 1.44 7.53 1.33 0.6 45.3 12.3 9.02 1.11 0.61 3.63 345.0 216.7 266.3 78.7 0.32 0.28 27.6
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_U20 CCZ05644 574801.0 6452798.0 0 0.3 0.3 18.4 2.9 105.5 50.5 38.3 6.25 3.97 1.39 7.23 1.35 0.57 45.7 12.2 8.94 1.1 0.57 3.64 345.8 216.2 267.2 78.6 0.32 0.28 27.5
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_V12 CCZ05645 574999.0 6454394.0 0 0.3 0.3 12.1 1.6 71.3 36.2 27.8 4.74 2.82 1.11 5.23 0.93 0.41 31.8 8.52 6.49 0.83 0.42 2.58 242.2 154.6 185.0 57.2 0.33 0.28 27.8
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_V13 CCZ05646 575001.0 6454190.0 0 0.3 0.3 15.0 2.2 105 50.3 44.2 7.19 4.65 1.25 7.83 1.55 0.67 45.2 12.1 8.95 1.24 0.66 4.09 355.3 226.3 265.7 89.6 0.34 0.27 27.1
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_V14 CCZ05647 574999.0 6453995.0 0 0.3 0.3 12.7 1.9 72.8 37.3 38.3 6.21 3.82 1.32 6.08 1.32 0.56 32.9 9.01 6.89 0.99 0.57 3.78 267.4 177.9 190.4 76.9 0.36 0.27 27.1
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_V15 CCZ05648 574999.0 6453792.0 0 0.3 0.3 15.8 3.3 130.5 64.6 63 10.85 6.35 2.31 11.9 2.23 0.88 62 16.3 13.05 1.84 0.97 5.99 473.0 312.7 343.2 129.8 0.36 0.29 28.6
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_V16 CCZ05649 575004.0 6453591.0 0 0.3 0.3 16.2 2.7 100 49.9 39.1 6.6 4.1 1.33 7.36 1.37 0.62 43.5 11.6 8.71 1.1 0.61 3.81 336.8 213.9 256.2 80.5 0.33 0.27 27.4
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_V17 CCZ05650 575000.0 6453393.0 0 0.3 0.3 14.5 2.3 88.5 45.1 36.8 6.15 3.83 1.35 6.56 1.32 0.55 40.8 10.6 7.87 1.02 0.55 3.52 306.4 197.7 231.1 75.3 0.34 0.28 27.9
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_V18 CCZ05651 575001.0 6453195.0 0 0.3 0.3 14.5 2.4 80 40 31.4 5.28 3.21 1.23 5.69 1.09 0.46 34.6 9.37 7.09 0.9 0.49 3.18 269.7 171.4 205.1 64.6 0.33 0.27 27.3
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_V19 CCZ05652 574999.0 6452991.0 0 0.3 0.3 13.1 2.2 73.9 36.6 31.2 5.23 3.23 1.04 5.29 1.08 0.49 32 8.7 6.42 0.88 0.49 3.14 252.6 161.8 189.0 63.6 0.34 0.27 27.1
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_V20 CCZ05653 575001.0 6452793.0 0 0.3 0.3 15.2 2.2 82.2 41.6 34.3 5.31 3.46 1.07 5.99 1.13 0.49 36.5 9.89 7.19 0.86 0.5 3.22 281.5 180.5 212.6 68.9 0.34 0.27 27.3
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_W12 CCZ05654 575202.0 6454400.0 0 0.3 0.3 16.3 2.3 93.7 45.8 39.4 6.58 4.06 1.37 7.54 1.43 0.57 42.3 11.35 8.53 1.16 0.61 3.97 323.1 208.0 241.8 81.4 0.34 0.28 28.0
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_W13 CCZ05655 575203.0 6454197.0 0 0.3 0.3 19.5 2.4 91.8 43.7 41.6 6.6 4.21 1.24 7.31 1.43 0.63 39.8 10.8 8.39 1.1 0.64 4.12 317.4 204.6 233.2 84.1 0.35 0.27 27.3
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_W14 CCZ05656 575203.0 6453997.0 0 0.3 0.3 13.2 2.3 93.2 46.2 40 6.6 4.11 1.41 7.1 1.44 0.58 41.3 11.05 8.3 1.1 0.58 3.75 321.2 206.8 239.8 81.4 0.34 0.27 27.5
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_W15 CCZ05657 575200.0 6453793.0 0 0.3 0.3 12.5 2.4 106 50.7 49 8.36 4.86 1.79 9.19 1.71 0.71 47.7 12.05 10.15 1.45 0.73 4.46 372.1 241.9 271.6 100.4 0.35 0.28 27.9
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_W16 CCZ05658 575203.0 6453593.0 0 0.3 0.3 15.8 2.7 102.5 52.5 42.6 6.76 4.16 1.46 7.46 1.4 0.67 44.8 12.2 9.06 1.2 0.67 4.17 351.2 225.3 265.0 86.2 0.33 0.27 27.1
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_W17 CCZ05659 575198.0 6453396.0 0 0.3 0.3 14.6 2.1 90.2 47.8 30.3 5.44 3.08 1.5 6.4 1.08 0.43 42.7 11.85 8.4 0.94 0.47 2.71 304.5 193.7 240.7 63.8 0.32 0.29 29.1
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_W18 CCZ05660 575201.0 6453200.0 0 0.3 0.3 15.7 3.0 98.4 52.8 38.7 6.24 4 1.44 7.08 1.36 0.58 43.3 11.8 8.71 1.06 0.61 3.95 337.0 216.2 257.7 79.4 0.33 0.27 27.1
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_W19 CCZ05661 575204.0 6452996.0 0 0.3 0.3 12.4 1.9 69.2 35.5 34 5.23 3.68 1.21 5.16 1.15 0.61 32.4 8.49 6.17 0.81 0.59 3.75 250.5 165.5 181.8 68.6 0.36 0.27 27.2
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_W20 CCZ05662 575202.0 6452795.0 0 0.3 0.3 13.7 2.4 58.2 32 28.9 4.49 3.02 0.95 4.72 0.96 0.47 26.4 7.33 5.19 0.7 0.45 3.13 213.1 141.6 154.7 58.4 0.35 0.27 26.8
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_X12 CCZ05663 575399.0 6454396.0 0 0.3 0.3 19.3 2.3 109 52.7 54.8 8.73 6.03 1.34 8.22 1.9 0.84 45.7 12.4 9.23 1.34 0.92 5.47 384.2 250.3 274.7 109.5 0.35 0.26 26.0
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_X13 CCZ05664 575400.0 6454192.0 0 0.3 0.3 15.4 3.0 99 48 51.2 8.67 5.28 1.3 8.88 1.83 0.74 44.1 11.7 9.48 1.51 0.81 4.8 358.3 236.7 254.5 103.9 0.36 0.27 27.5
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_X14 CCZ05665 575402.0 6453996.0 0 0.3 0.3 20.7 3.3 153 82.7 56.1 9.61 5.75 1.85 9.91 2.06 0.86 62.8 17.2 12.25 1.62 0.83 5.35 507.9 319.9 393.2 114.7 0.31 0.26 26.1
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_X15 CCZ05666 575400.0 6453795.0 0 0.3 0.3 15.6 2.6 98.8 50.4 34.2 5.79 3.24 1.36 6.92 1.18 0.47 42.2 11.35 8.32 1 0.49 3.09 323.5 202.2 253.1 70.5 0.32 0.27 27.3
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_X16 CCZ05667 575399.0 6453591.0 0 0.3 0.3 15.1 2.8 112.5 59.4 42.4 7.17 4.39 1.72 8.12 1.48 0.62 49.2 13.3 9.16 1.21 0.66 4.07 379.6 241.4 291.9 87.7 0.32 0.27 27.2
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_X17 CCZ05668 575402.0 6453394.0 0 0.3 0.3 13.7 2.3 98.5 49.7 32.3 5.61 3.28 1.55 6.79 1.16 0.49 43.3 11.75 8.75 1.01 0.47 3.27 322.3 201.3 254.1 68.2 0.31 0.28 28.0
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_X18 CCZ05669 575404.0 6453192.0 0 0.3 0.3 13.9 2.5 126.5 53.2 45.3 7.54 5 1.95 8.49 1.59 0.76 53.9 13.7 11 1.3 0.74 4.77 404.4 249.0 310.0 94.4 0.33 0.28 27.7
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_X19 CCZ05670 575398.0 6452993.0 0 0.3 0.3 17.1 2.7 106.5 50.9 37.6 6.32 3.96 1.52 7.16 1.28 0.56 44.9 12.25 8.79 1.07 0.54 3.71 345.6 214.8 267.9 77.7 0.32 0.27 27.2
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_X20 CCZ05671 575400.0 6452792.0 0 0.3 0.3 14.7 2.5 96.4 47.4 37.4 5.94 3.85 1.5 6.75 1.28 0.58 41.6 11.45 8.28 1.03 0.59 3.64 322.4 203.9 246.0 76.4 0.33 0.27 27.2
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_Y12 CCZ05672 575600.0 6454397.0 0 0.3 0.3 18.1 2.5 111.5 57.8 45.3 8.02 4.8 1.54 8.88 1.63 0.63 52.8 14.2 10.35 1.36 0.71 4.23 389.5 252.6 295.5 94.0 0.34 0.29 28.7
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_Y13 CCZ05673 575592.0 6454191.0 0 0.3 0.3 11.1 2.5 102 51.6 42.3 7.62 4.41 1.46 8.1 1.51 0.65 46.3 11.95 9.22 1.26 0.69 4.13 352.9 227.6 264.9 88.0 0.34 0.28 28.0
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_Y14 CCZ05674 575600.0 6453999.0 0 0.3 0.3 18.3 2.9 125.5 63.1 50.9 8.5 5.34 1.58 8.97 1.79 0.83 52.2 14.55 10.6 1.46 0.78 4.88 422.8 268.6 318.9 103.8 0.33 0.27 26.6
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_Y15 CCZ05675 575599.0 6453797.0 0 0.3 0.3 14.3 2.7 112 59.1 41.9 6.45 4.12 1.5 7.47 1.36 0.62 49.2 13.3 9.14 1.18 0.62 3.87 375.4 237.8 290.9 84.4 0.32 0.27 27.0
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_Y16 CCZ05676 575600.0 6453598.0 0 0.3 0.3 16.2 2.6 100.5 52.4 29.2 4.77 2.82 1.26 5.89 0.98 0.4 43.1 12.1 8 0.89 0.45 2.73 319.4 195.9 259.1 60.3 0.30 0.27 27.4
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_Y17 CCZ05677 575600.0 6453400.0 0 0.3 0.3 12.7 2.2 77.4 40.6 35.4 5.79 3.5 1.33 6.34 1.18 0.49 36.2 9.73 7.52 0.96 0.53 3.45 277.4 182.3 205.4 72.0 0.35 0.28 28.0
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_Y18 CCZ05678 575598.0 6453200.0 0 0.3 0.3 17.8 2.8 107.5 53.5 36.4 6.05 3.51 1.59 7.03 1.28 0.51 47.6 12.55 8.92 1.08 0.55 3.43 350.8 218.7 275.8 75.0 0.32 0.28 27.7
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_Y19 CCZ05679 575600.0 6452995.0 0 0.3 0.3 18.4 2.8 105 55.9 40.4 6.74 3.94 1.53 7.72 1.38 0.6 49.9 13.7 9.87 1.14 0.63 3.8 363.6 234.6 280.7 82.9 0.33 0.29 28.7
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_Y20 CCZ05680 575598.0 6452799.0 0 0.3 0.3 19.3 2.8 115 56 37.4 6.46 3.52 1.33 7.56 1.26 0.52 51.4 13.65 9.9 1.14 0.55 3.27 371.8 230.5 294.9 76.9 0.32 0.28 28.3
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_Z12 CCZ05681 575795.0 6454397.0 0 0.3 0.3 17.7 2.8 126.5 65.3 61.7 9.72 5.93 1.61 10.45 2.09 0.82 58.5 15.85 11.7 1.71 0.88 5.55 455.8 300.4 332.9 122.9 0.35 0.28 27.7
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_Z13 CCZ05682 575791.0 6454200.0 0 0.3 0.3 14.1 2.8 113.5 58.9 52.5 8.7 5.3 1.83 9.14 1.89 0.75 52.3 13.75 10.15 1.5 0.82 4.83 404.5 265.1 297.9 106.6 0.35 0.28 27.6
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_Z14 CCZ05683 575806.0 6453995.0 0 0.3 0.3 14.3 2.0 85.7 43.9 36.2 6.8 3.96 1.48 6.8 1.34 0.5 41.2 11 8.07 1.16 0.59 3.6 303.6 198.3 227.5 76.1 0.35 0.29 28.9
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_Z15 CCZ05684 575799.0 6453795.0 0 0.3 0.3 13.1 2.9 129 66.4 32.1 5.82 3.12 1.54 7.34 1.11 0.4 51.4 15.1 9.37 1.12 0.43 2.8 393.4 234.9 325.4 68.0 0.28 0.27 26.8
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_Z16 CCZ05685 575799.0 6453594.0 0 0.3 0.3 12.9 2.5 78.7 39.8 30.8 5.46 3.33 1.33 5.92 1.2 0.46 36.5 9.66 7.18 0.96 0.48 3.1 270.6 173.9 205.9 64.7 0.33 0.28 28.4
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_Z17 CCZ05686 575797.0 6453396.0 0 0.3 0.3 12.4 2.3 83.3 45.3 44.8 6.7 4.24 1.61 7.39 1.49 0.62 41.2 10.75 8.02 1.18 0.61 3.91 314.6 212.2 225.8 88.8 0.37 0.28 28.0
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_Z18 CCZ05687 575798.0 6453193.0 0 0.3 0.3 17.2 2.7 111.5 54 49 7.87 5 1.77 8.66 1.69 0.72 48.5 13 9.51 1.33 0.76 4.85 383.3 246.4 283.6 99.7 0.34 0.27 27.1
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_Z19 CCZ05688 575802.0 6452992.0 0 0.3 0.3 18.1 3.0 108 55.1 45.8 7.17 4.48 1.29 7.39 1.53 0.65 47.6 13.1 8.86 1.26 0.72 4.4 370.2 237.6 278.9 91.3 0.34 0.27 27.0
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_Z20 CCZ05689 575800.0 6452800.0 0 0.3 0.3 17.3 2.7 118.5 60.5 35.5 6 3.5 1.42 7.06 1.2 0.49 50.2 14.25 9.27 1.07 0.53 3.32 376.4 230.8 303.0 73.3 0.30 0.27 27.3
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AA12 CCZ05690 576000.0 6454400.0 0 0.3 0.3 13.0 2.0 86.6 44.2 42.2 6.77 4.39 1.26 7.2 1.49 0.59 40.6 10.5 8.41 1.22 0.64 3.95 313.2 206.8 228.0 85.2 0.36 0.28 27.9
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AA13 CCZ05691 576002.0 6454198.0 0 0.3 0.3 13.7 2.0 100.5 54.3 41.8 7.15 4.24 1.64 7.97 1.53 0.59 49.3 13.35 9.68 1.32 0.63 3.93 358.4 234.9 272.0 86.4 0.34 0.29 29.0
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AA14 CCZ05692 575997.0 6453998.0 0 0.3 0.3 15.0 2.9 107.5 53.9 36.6 6.55 4.24 1.34 7.24 1.42 0.55 46.4 12.65 9.51 1.18 0.56 4.08 353.4 221.3 275.7 77.7 0.31 0.28 27.6
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AA15 CCZ05693 575999.0 6453799.0 0 0.3 0.3 10.4 3.3 130.5 65.2 39.8 7.79 4.09 1.94 8.2 1.51 0.47 57.6 15.4 9.7 1.21 0.66 3.95 418.6 258.3 333.8 84.8 0.31 0.28 27.9
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AA16 CCZ05694 576003.0 6453601.0 0 0.3 0.3 13.7 2.1 85 44.6 30.6 5.37 3.05 1.38 6.23 1.06 0.44 38.5 10.5 7.5 0.93 0.46 2.89 286.9 182.5 223.0 63.9 0.32 0.28 28.1
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AA17 CCZ05695 575999.0 6453398.0 0 0.3 0.3 12.0 2.1 72.6 38 29.7 5.09 2.99 1.14 5.74 1.04 0.46 33.4 8.92 6.18 0.89 0.44 2.79 252.0 162.8 190.7 61.4 0.34 0.28 27.9
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AA18 CCZ05696 575999.0 6453197.0 0 0.3 0.3 15.3 2.6 92.9 48.1 40.7 6.28 3.88 1.33 6.74 1.32 0.63 42.6 11.5 8.04 1.12 0.63 4.03 324.9 210.8 243.4 81.5 0.34 0.27 27.5
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AA19 CCZ05697 576006.0 6453003.0 0 0.3 0.3 17.3 2.8 106.5 54.2 33.3 5.53 3.12 1.39 7.01 1.13 0.45 46.4 12.75 8.77 1.07 0.49 2.93 342.9 212.1 274.1 68.9 0.31 0.28 27.8
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AA20 CCZ05698 576002.0 6452797.0 0 0.3 0.3 13.4 2.2 84.2 44.4 28.4 4.58 2.85 1.46 5.98 0.94 0.41 38.6 10.65 7.17 0.9 0.42 2.63 280.9 177.5 221.7 59.2 0.32 0.28 28.3
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AB12 CCZ05699 576200.0 6454398.0 0 0.3 0.3 17.9 2.6 107.5 54 45.8 7.49 4.82 1.27 8.23 1.52 0.63 49 13.4 9.79 1.36 0.72 4.47 373.3 241.2 280.1 93.2 0.34 0.28 28.0
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AB13 CCZ05700 576202.0 6454197.0 0 0.3 0.3 14.8 2.1 91.3 48 37.5 6.21 3.66 1.42 7.19 1.33 0.54 42.5 11.3 8.53 1.1 0.56 3.45 318.4 206.3 241.6 76.9 0.34 0.28 28.2
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AB14 CCZ05701 576201.0 6453998.0 0 0.3 0.3 13.8 2.4 105.5 57.5 37.7 6.32 3.64 1.68 7.73 1.29 0.48 48.3 13.15 9.83 1.18 0.53 3.27 358.5 228.9 280.7 77.9 0.32 0.28 28.2
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AB15 CCZ05702 576201.0 6453797.0 0 0.3 0.3 11.2 3.4 105 62.5 39.9 6.13 3.61 1.51 7.17 1.28 0.54 45.7 12.75 8.12 1.1 0.54 3.39 360.1 231.1 280.4 79.7 0.32 0.26 26.3
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AB16 CCZ05703 576200.0 6453598.0 0 0.3 0.3 14.0 2.5 87.8 45.4 27.4 4.54 2.82 1.2 5.8 0.96 0.4 39 10.7 6.88 0.9 0.45 2.7 285.0 177.1 227.5 57.5 0.31 0.28 27.8
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AB17 CCZ05704 576199.0 6453396.0 0 0.3 0.3 12.5 2.2 71.6 37.4 32 5.21 3.4 1.12 5.66 1.09 0.44 33.6 8.73 6.47 0.87 0.46 3.05 254.2 166.2 189.1 65.1 0.35 0.28 27.8
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AB18 CCZ05705 576200.0 6453195.0 0 0.3 0.3 18.8 3.2 117.5 60.1 58.4 9.2 5.97 1.63 8.77 1.98 0.92 51.2 14.25 9.62 1.54 0.96 5.71 419.2 274.8 302.9 116.3 0.35 0.26 26.4
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AB19 CCZ05706 576200.0 6452999.0 0 0.3 0.3 19.1 3.2 116 59.6 38 6.34 3.74 1.43 7.55 1.28 0.52 50.3 14.1 9.61 1.16 0.58 3.57 377.6 235.1 299.2 78.3 0.31 0.28 27.6
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AB20 CCZ05707 576198.0 6452797.0 0 0.3 0.3 18.3 3.2 109.5 56.5 36.6 5.95 3.55 1.43 7.49 1.22 0.52 47.2 12.85 8.51 1.09 0.55 3.5 356.8 222.3 281.2 75.5 0.31 0.27 27.2
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AC12 CCZ05708 576403.0 6454399.0 0 0.3 0.3 14.6 2.0 78.2 40.5 34.7 5.59 3.5 1.21 5.74 1.18 0.5 36.2 9.62 7.25 0.95 0.56 3.4 275.9 179.8 205.8 70.0 0.35 0.28 27.7
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AC13 CCZ05709 576402.0 6454197.0 0 0.3 0.3 11.2 1.8 89.1 46 31 5.27 3.16 1.63 6.34 1.08 0.43 40.6 11.25 8.08 0.99 0.5 2.87 298.7 189.2 233.7 65.0 0.32 0.28 28.4
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AC14 CCZ05710 576402.0 6453998.0 0 0.3 0.3 14.2 2.2 86.4 44.4 30.5 5.04 2.81 1.28 5.56 1.07 0.44 38.9 10.45 7.4 0.88 0.42 2.72 286.7 180.6 224.8 62.0 0.32 0.28 27.8
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AC15 CCZ05711 576400.0 6453794.0 0 0.3 0.3 11.8 3.9 143.5 72.2 43.3 7.85 4.42 1.94 9.23 1.61 0.6 60.7 15.65 11.2 1.38 0.63 4.12 455.1 278.9 363.6 91.5 0.30 0.27 27.2
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AC16 CCZ05712 576403.0 6453599.0 0 0.3 0.3 16.2 2.6 113 55.1 32.2 5.92 3.02 1.45 6.86 1.17 0.44 48.9 13 8.85 0.99 0.44 2.95 354.0 215.2 286.4 67.6 0.30 0.28 27.9
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AC17 CCZ05713 576402.0 6453397.0 0 0.3 0.3 15.8 2.3 101 50.8 36.2 6.39 3.55 1.56 7.35 1.33 0.48 46.8 12.2 8.94 1.09 0.51 3.34 338.7 214.7 263.3 75.4 0.33 0.29 28.6
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AC18 CCZ05714 576401.0 6453199.0 0 0.3 0.3 15.7 2.7 102 50.8 44.5 7.27 4.54 1.28 7.67 1.57 0.67 46.5 11.85 8.65 1.16 0.65 4.42 353.5 228.2 263.5 90.1 0.34 0.27 27.5
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AC19 CCZ05715 576402.0 6452999.0 0 0.3 0.3 18.9 3.1 116.5 56.5 32.5 6.02 3.33 1.42 7.73 1.2 0.44 51.5 13.9 9.53 1.11 0.44 3.09 367.0 223.9 297.3 69.7 0.30 0.29 28.6
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AC20 CCZ05716 576398.0 6452800.0 0 0.3 0.3 20.2 3.7 229 115 38.4 7.22 3.71 2.02 9.82 1.41 0.5 89.7 25.5 14.7 1.4 0.49 3.34 651.8 370.5 568.7 83.1 0.25 0.27 26.7
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AD12 CCZ05717 576600.0 6454399.0 0 0.3 0.3 13.3 2.4 93.4 45.4 33.6 5.62 3.4 1.24 6.4 1.25 0.48 40.3 10.5 6.98 0.96 0.5 3.37 305.1 190.4 235.8 69.3 0.32 0.27 27.1
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AD13 CCZ05718 576602.0 6454197.0 0 0.3 0.3 11.7 2.0 87.8 44.2 37.8 7.21 4.01 1.62 7.6 1.36 0.48 44.6 11.75 8.29 1.22 0.58 3.58 315.3 207.4 235.5 79.8 0.35 0.30 29.9
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AD14 CCZ05719 576601.0 6453992.0 0 0.3 0.3 14.1 2.3 89.4 46 37.3 6.8 4.11 1.7 6.92 1.4 0.57 45 11.7 8.21 1.12 0.59 3.97 318.5 208.7 239.9 78.6 0.35 0.29 29.3
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AD15 CCZ05720 576602.0 6453794.0 0 0.3 0.3 12.3 3.9 93 52.4 28.1 5.2 3.25 1.34 6.16 1.06 0.39 40.9 11.2 7.4 0.93 0.46 2.88 306.1 191.9 245.5 60.6 0.30 0.27 27.4
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AD16 CCZ05721 576601.0 6453596.0 0 0.3 0.3 15.0 2.7 93 45.2 32.1 6.16 3.42 1.46 6.65 1.26 0.47 43.6 11.5 7.9 1.06 0.48 3.09 309.6 195.3 241.2 68.4 0.33 0.29 29.0
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AD17 CCZ05722 576600.0 6453393.0 0 0.3 0.3 17.1 2.9 114 53.6 40.4 7.1 4.41 1.6 7.79 1.38 0.59 50.8 13.4 9.16 1.17 0.59 3.78 372.9 232.9 289.0 83.9 0.33 0.28 28.0
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AD18 CCZ05723 576602.0 6453193.0 0 0.3 0.3 20.1 3.3 124.5 61.3 42.1 7.57 4.49 1.58 8.14 1.46 0.61 56.6 15.75 10.35 1.38 0.6 3.94 409.5 256.6 321.9 87.7 0.32 0.29 28.5
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AD19 CCZ05724 576599.0 6452995.0 0 0.3 0.3 21.3 3.8 145 70.6 40.8 7.01 3.87 1.61 8.29 1.41 0.52 62.1 16.6 11.4 1.24 0.57 3.85 451.0 272.9 366.6 84.4 0.30 0.28 27.7
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AD20 CCZ05725 576600.0 6452793.0 0 0.3 0.3 20.7 3.8 153.5 75.7 41 7.44 4.05 1.77 8.8 1.48 0.59 65.1 17.5 11.25 1.32 0.57 3.67 473.6 285.1 387.5 86.2 0.30 0.28 27.5
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AE12 CCZ05726 576799.0 6454395.0 0 0.3 0.3 13.5 1.8 78.4 39.5 30.4 5.28 3.17 1.22 6.08 1.09 0.44 38.1 9.65 6.89 0.87 0.44 3 270.1 173.8 206.7 63.4 0.34 0.29 28.9
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AE13 CCZ05727 576803.0 6454195.0 0 0.3 0.3 15.4 2.3 104 51.4 37.5 6.69 3.86 1.52 7.17 1.38 0.51 47.9 12.55 9.12 1.14 0.54 3.49 347.5 219.7 269.6 77.8 0.33 0.28 28.5
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AE14 CCZ05728 576803.0 6453996.0 0 0.3 0.3 15.1 2.4 101.5 51.5 34.7 6.15 3.59 1.4 7.13 1.27 0.54 46.3 11.9 8.5 1.09 0.51 3.35 336.1 211.5 263.3 72.8 0.32 0.28 28.2
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AE15 CCZ05729 576802.0 6453796.0 0 0.3 0.3 12.4 2.2 78.4 40.3 28.3 4.86 2.88 1.16 5.53 1.01 0.39 35.6 9.42 6.97 0.84 0.42 2.64 263.2 166.9 204.6 58.6 0.32 0.28 28.1
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AE16 CCZ05730 576800.0 6453594.0 0 0.3 0.3 14.1 2.7 120 55.6 48.3 7.72 4.79 1.66 7.99 1.76 0.74 52 13.45 9.33 1.3 0.73 4.79 397.8 250.4 300.3 97.5 0.34 0.27 27.0
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AE17 CCZ05731 576803.0 6453397.0 0 0.3 0.3 15.1 2.6 119.5 55.8 35.6 6.22 3.66 1.52 7.33 1.29 0.46 52.1 13.55 9.36 1.1 0.49 3.29 374.6 227.8 300.2 74.3 0.31 0.28 28.0
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AE18 CCZ05732 576802.0 6453196.0 0 0.3 0.3 22.1 3.4 147 69.4 40.2 7.46 3.9 1.6 8.73 1.42 0.53 62.3 16.6 11.25 1.28 0.56 3.7 452.3 271.7 367.7 84.6 0.30 0.28 27.8
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AE19 CCZ05733 576805.0 6453000.0 0 0.3 0.3 20.1 3.5 167 77.4 37.6 6.71 3.65 1.68 8.65 1.4 0.5 68 18.4 11.75 1.26 0.55 3.6 491.0 285.9 411.1 79.9 0.28 0.27 27.4
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AE20 CCZ05734 576803.0 6452797.0 0 0.3 0.3 20.9 3.7 134 64.4 48.5 8 4.98 1.55 8.49 1.66 0.76 58.8 15.4 10.15 1.26 0.79 5.08 438.1 273.5 339.1 99.0 0.33 0.27 27.3
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AF12 CCZ05735 577004.0 6454394.0 0 0.3 0.3 15.0 2.1 88.3 42.7 38 6.3 3.83 1.2 6.62 1.36 0.53 40.4 10.45 7.3 1.02 0.57 3.83 304.0 195.6 226.8 77.3 0.35 0.28 27.7
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AF13 CCZ05736 577002.0 6454198.0 0 0.3 0.3 16.7 2.8 138 64.4 42.6 7.64 4.23 1.67 8.67 1.56 0.66 60.7 16.05 10.9 1.32 0.63 3.9 436.8 267.2 347.9 88.9 0.31 0.28 28.2
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AF14 CCZ05737 577001.0 6453993.0 0 0.3 0.3 15.2 2.9 105 51.5 29.8 5.56 3.04 1.26 6.42 1.15 0.41 44.9 11.95 7.82 0.97 0.45 2.77 328.4 199.4 265.3 63.2 0.30 0.28 27.6
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AF15 CCZ05738 577001.0 6453795.0 0 0.3 0.3 15.6 2.6 113 57.1 34 6.15 3.24 1.44 7.25 1.18 0.44 51.2 13.5 9.06 1.07 0.45 3.08 363.4 224.6 292.3 71.1 0.31 0.28 28.4
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AF16 CCZ05739 577001.0 6453595.0 0 0.3 0.3 16.9 2.7 125.5 61.7 36.8 6.77 3.87 1.66 8.06 1.36 0.46 55.8 14.7 10.05 1.24 0.5 3.42 399.2 245.0 321.0 78.1 0.31 0.28 28.3
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AF17 CCZ05740 577003.0 6453394.0 0 0.3 0.3 18.6 3.6 122.5 60 53.5 8.35 5.75 1.37 8.18 1.88 0.82 53.1 14 9.46 1.32 0.87 5.57 417.8 267.3 310.7 107.1 0.34 0.26 26.4
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AF18 CCZ05741 577004.0 6453196.0 0 0.3 0.3 20.0 3.2 135 66.3 37.2 6.58 3.71 1.51 8.01 1.35 0.48 59 15.85 10.6 1.22 0.5 3.22 421.6 255.8 343.9 77.8 0.30 0.28 28.1
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AF19 CCZ05742 577001.0 6452996.0 0 0.3 0.3 21.8 3.9 146.5 72.1 42.6 7.7 4.28 1.8 9.27 1.55 0.58 64 17.05 12.05 1.33 0.63 4.03 463.6 283.7 373.7 89.9 0.30 0.28 28.1
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AF20 CCZ05743 577004.0 6452793.0 0 0.3 0.3 16.9 3.0 106 51.8 33.3 6.01 3.13 1.43 6.8 1.17 0.42 46.6 12.35 8.63 1 0.44 3.03 339.5 209.2 270.2 69.2 0.31 0.28 28.0
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AG12 CCZ05744 577200.0 6454399.0 0 0.3 0.3 12.5 2.0 93.3 44.8 41.4 7.32 4.16 1.34 7.5 1.49 0.58 42.9 11.15 8.26 1.2 0.59 3.84 325.0 210.4 240.2 84.8 0.35 0.28 28.2
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AG13 CCZ05745 577200.0 6454200.0 0 0.3 0.3 19.0 2.7 106 52.9 37.7 6.73 4.23 1.4 7.36 1.36 0.55 48.9 12.5 9.34 1.26 0.57 3.82 354.4 224.2 275.2 79.2 0.33 0.28 28.4
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AG14 CCZ05746 577201.0 6454000.0 0 0.3 0.3 17.9 3.0 123.5 60.3 33.9 5.78 3.42 1.59 7.59 1.26 0.47 53 13.9 9.17 1.12 0.48 3.33 383.5 231.8 311.7 71.8 0.30 0.28 27.6
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AG15 CCZ05747 577201.0 6453800.0 0 0.3 0.3 16.7 2.8 112 53.8 35.5 6.35 3.73 1.46 7.36 1.3 0.51 47.3 12.75 9.41 1.14 0.57 3.71 357.3 219.7 282.2 75.1 0.31 0.28 27.6
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AG16 CCZ05748 577203.0 6453597.0 0 0.3 0.3 15.6 2.4 101 49 32.4 5.78 3.45 1.27 6.2 1.2 0.47 43.6 11.6 8.09 1.03 0.51 3.23 323.5 199.4 255.8 67.7 0.31 0.28 27.6
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AG17 CCZ05749 577202.0 6453396.0 0 0.3 0.3 15.7 2.8 101 50.3 47.5 7.56 5.04 1.53 7.37 1.7 0.71 45 11.95 8.97 1.18 0.76 4.88 356.0 231.9 260.4 95.6 0.35 0.27 26.9
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AG18 CCZ05750 577202.0 6453199.0 0 0.3 0.3 15.5 2.9 106 53.2 37.3 6.15 3.85 1.48 6.86 1.32 0.62 45.7 12.15 8.25 1.08 0.6 3.96 347.3 217.1 270.2 77.1 0.32 0.27 27.0
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AG19 CCZ05751 577202.0 6452995.0 0 0.3 0.3 19.1 3.3 121 58.9 47.8 7.8 4.7 1.52 7.97 1.6 0.72 51.9 14.1 9.84 1.28 0.72 4.65 402.9 254.3 306.7 96.2 0.33 0.27 27.0
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AG20 CCZ05752 577203.0 6452796.0 0 0.3 0.3 17.9 3.3 104.5 50.2 38.9 6.49 3.94 1.37 6.88 1.37 0.62 45.4 11.9 8.61 1.14 0.58 3.79 344.0 215.7 264.6 79.5 0.33 0.27 27.3
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AH12 CCZ05753 577402.0 6454398.0 0 0.3 0.3 13.2 1.9 80.5 40 29.1 5.13 3.13 1.28 5.87 1.06 0.44 37 9.63 7.38 0.88 0.45 2.83 270.3 171.4 209.1 61.2 0.33 0.29 28.5
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AH13 CCZ05754 577399.0 6454196.0 0 0.3 0.3 14.3 2.7 89.2 43.9 32.5 5.66 3.52 1.31 5.73 1.14 0.47 39.3 10.4 7.56 0.98 0.5 3.41 295.6 186.0 228.2 67.4 0.33 0.28 27.5
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AH14 CCZ05755 577399.0 6453998.0 0 0.3 0.3 16.4 2.7 93.3 46.3 28.9 5.21 2.92 1.28 6 1.04 0.39 41.4 10.5 7.77 0.9 0.45 2.69 299.6 185.0 238.9 60.7 0.31 0.28 28.0
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AH15 CCZ05756 577400.0 6453799.0 0 0.3 0.3 15.7 3.7 131.5 64.8 37 6.96 3.87 1.75 8.12 1.38 0.52 57.6 15.35 10.4 1.17 0.53 3.41 414.1 252.6 335.3 78.8 0.30 0.28 28.1
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AH16 CCZ05757 577397.0 6453596.0 0 0.3 0.3 17.1 2.9 111 55.6 42.8 7.15 4.25 1.6 8.05 1.5 0.66 50.7 13.15 9.63 1.22 0.67 4.37 375.9 239.6 287.8 88.2 0.33 0.28 28.0
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AH17 CCZ05758 577401.0 6453397.0 0 0.3 0.3 14.4 2.4 110 54.2 36.7 6.4 3.71 1.53 7.31 1.32 0.53 48.7 12.8 9.22 1.1 0.53 3.48 358.0 222.9 281.7 76.4 0.32 0.28 27.9
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AH18 CCZ05759 577402.0 6453194.0 0 0.3 0.3 18.9 3.2 149 70.6 34.4 6.46 3.47 1.69 8.13 1.3 0.46 61.7 16.6 11.2 1.15 0.51 3.18 444.8 261.8 370.8 74.0 0.28 0.28 27.7
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AH19 CCZ05760 577398.0 6452998.0 0 0.3 0.3 19.6 3.8 121 58.9 51.7 8.19 5.42 1.56 8.45 1.84 0.84 52.4 13.9 10.55 1.36 0.81 5.43 412.4 263.8 307.9 104.6 0.34 0.27 26.9
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AH20 CCZ05761 577395.0 6452801.0 0 0.3 0.3 17.9 2.9 107.5 52.7 38.1 6.63 3.9 1.54 7.3 1.34 0.52 47 12.25 8.94 1.16 0.6 3.78 353.0 220.9 273.8 79.1 0.32 0.28 27.6
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AI12 CCZ05762 577600.0 6454397.0 0 0.3 0.3 16.3 2.1 101 49 35.8 6.42 3.8 1.46 6.99 1.34 0.52 45.3 11.8 9.08 1.08 0.58 3.61 334.3 210.2 259.2 75.1 0.32 0.28 28.2
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AI13 CCZ05763 577601.0 6454195.0 0 0.3 0.3 16.5 2.7 117.5 64.2 46.1 8.03 4.82 1.69 9.28 1.67 0.76 57.9 15.25 11 1.4 0.73 4.63 414.8 270.5 318.3 96.5 0.33 0.29 29.0
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AI14 CCZ05764 577601.0 6453997.0 0 0.3 0.3 16.4 2.8 99.7 48.7 33.6 6.19 3.34 1.35 6.59 1.18 0.49 43.1 11.5 8.36 0.98 0.49 3.54 323.9 201.4 253.4 70.4 0.32 0.28 27.7
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AI15 CCZ05765 577603.0 6453799.0 0 0.3 0.3 15.5 3.0 125.5 60.9 34.6 6.23 3.5 1.64 7.49 1.22 0.48 56.5 14.85 10.25 1.12 0.55 3.45 394.8 240.6 321.3 73.4 0.30 0.29 28.6
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AI16 CCZ05766 577602.0 6453600.0 0 0.3 0.3 18.7 2.8 108.5 56.2 38.2 6.75 3.89 1.6 7.58 1.42 0.58 51.3 13.6 9.96 1.15 0.61 3.84 367.0 233.7 287.0 80.0 0.33 0.29 28.8
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AI17 CCZ05767 577600.0 6453400.0 0 0.3 0.3 17.0 2.7 109.5 53.1 32.8 5.93 3.35 1.52 7.01 1.24 0.51 46.3 12.4 9.23 1.01 0.51 3.32 346.2 211.6 276.5 69.7 0.30 0.28 27.7
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AI18 CCZ05768 577599.0 6453198.0 0 0.3 0.3 18.6 3.6 139 67.9 42.5 7.56 4.35 1.67 8.37 1.62 0.63 56.9 15 10.5 1.28 0.63 4.26 435.9 265.2 347.0 88.9 0.30 0.27 26.7
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AI19 CCZ05769 577601.0 6452999.0 0 0.3 0.3 14.6 2.3 90.8 45.1 33.9 5.96 3.34 1.33 6.26 1.2 0.47 41.9 10.8 8.2 0.98 0.51 3.4 305.8 194.3 235.9 70.0 0.33 0.28 28.3
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AI20 CCZ05770 577602.0 6452799.0 0 0.3 0.3 16.0 2.7 97.8 47.2 34.2 5.84 3.35 1.3 6.31 1.18 0.5 41.9 11.2 8.54 0.98 0.51 3.08 317.7 197.6 247.8 69.9 0.32 0.28 27.5
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AJ12 CCZ05771 577802.0 6454397.0 0 0.3 0.3 12.6 2.0 78.9 38.9 33.8 5.67 3.39 1.29 5.94 1.19 0.53 36.9 9.32 7.25 0.94 0.5 3.31 274.3 177.4 205.3 69.1 0.35 0.28 28.1
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AJ13 CCZ05772 577802.0 6454194.0 0 0.3 0.3 13.8 2.2 93.2 45.9 32.7 6.14 3.36 1.36 6.75 1.16 0.46 44.2 11.55 8.74 1 0.5 3.29 313.1 198.6 244.0 69.1 0.33 0.29 29.3
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AJ14 CCZ05773 577800.0 6454000.0 0 0.3 0.3 14.8 2.9 98.6 50 35 6.17 3.66 1.3 6.43 1.29 0.48 44.3 11.7 8.41 0.99 0.56 3.49 327.8 206.6 255.3 72.4 0.32 0.28 27.8
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AJ15 CCZ05774 577802.0 6453794.0 0 0.3 0.3 13.9 2.5 81.6 40.2 31.3 5.21 3.2 1.19 5.8 1.1 0.45 37 9.52 6.72 0.88 0.46 3.14 274.2 174.0 209.8 64.4 0.33 0.28 27.8
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AJ16 CCZ05775 577803.0 6453599.0 0 0.3 0.3 14.5 2.5 88.9 44.6 36.4 6.13 3.65 1.32 6.35 1.25 0.57 39.9 10.15 7.7 0.95 0.57 3.85 303.8 194.6 229.2 74.5 0.34 0.27 27.4
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AJ17 CCZ05776 577803.0 6453395.0 0 0.3 0.3 14.8 2.3 96.4 47 33 5.82 3.31 1.39 6.5 1.2 0.44 42.4 11 8.65 1.05 0.5 3.26 315.2 196.8 246.3 68.9 0.32 0.28 28.0
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AJ18 CCZ05777 577803.0 6453196.0 0 0.3 0.3 18.7 3.1 132.5 64.1 35.3 6.35 3.33 1.52 7.66 1.26 0.46 56 15.05 10.3 1.12 0.55 3.26 407.5 244.8 333.4 74.1 0.30 0.28 27.7
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AJ19 CCZ05778 577804.0 6452998.0 0 0.3 0.3 15.4 2.6 97.9 46.9 36.8 6.15 3.87 1.35 6.76 1.26 0.63 42.8 11.1 7.96 1.06 0.61 3.84 323.9 203.6 247.8 76.0 0.33 0.27 27.4
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AJ20 CCZ05779 577806.0 6452797.0 0 0.3 0.3 19.0 2.7 109 52.8 35.3 6.32 3.35 1.48 7.78 1.26 0.52 48.7 12.7 9.08 1.08 0.49 3.26 352.7 218.8 278.5 74.2 0.32 0.28 28.4
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AK12 CCZ05780 577999.0 6454401.0 0 0.3 0.3 15.1 2.5 89.1 43.1 34.2 5.45 3.5 1.28 6.25 1.21 0.51 40.5 10.8 8.19 0.93 0.5 3.46 299.7 190.3 229.8 69.9 0.33 0.28 28.1
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AK13 CCZ05781 578003.0 6454202.0 0 0.3 0.3 12.2 2.1 76.3 37.2 29.2 5.03 2.85 1.3 5.37 1.01 0.45 34.7 9.07 7.09 0.86 0.45 2.97 257.4 163.7 197.0 60.4 0.33 0.28 28.2
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AK14 CCZ05782 578000.0 6454000.0 0 0.3 0.3 14.0 2.6 94.4 46 42.1 6.87 4.39 1.4 6.2 1.49 0.69 41.3 10.95 7.87 1.08 0.67 4.71 325.5 209.5 240.4 85.0 0.35 0.27 26.7
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AK15 CCZ05783 578003.0 6453798.0 0 0.3 0.3 14.9 2.4 96.6 47.6 34.8 6.12 3.56 1.52 6.82 1.25 0.57 43.5 11.6 8.91 1.04 0.51 3.39 322.2 203.6 249.6 72.7 0.33 0.28 28.3
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AK16 CCZ05784 578001.0 6453601.0 0 0.3 0.3 14.9 2.4 99.5 48.8 37 6.11 3.69 1.48 6.92 1.27 0.54 44.1 11.9 8.58 1.06 0.55 3.53 331.1 208.9 255.2 75.9 0.33 0.28 27.8
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AK17 CCZ05785 578003.0 6453400.0 0 0.3 0.3 14.8 2.4 90.3 44.7 35.8 5.99 3.79 1.5 6.32 1.29 0.6 40.6 10.75 7.96 0.97 0.57 3.98 307.1 196.2 232.9 74.2 0.33 0.28 27.6
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AK18 CCZ05786 578001.0 6453200.0 0 0.3 0.3 16.7 2.8 105.5 54.8 37.9 6.53 3.83 1.45 6.98 1.32 0.59 45.5 12.2 8.79 1.06 0.56 3.87 350.1 220.5 271.9 78.2 0.32 0.27 27.1
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AK19 CCZ05787 578003.0 6452998.0 0 0.3 0.3 16.6 2.5 102.5 49.2 34.9 6.03 3.59 1.42 7.02 1.27 0.46 46 12.3 8.74 1.02 0.48 3.33 334.9 209.0 262.3 72.6 0.32 0.28 28.3
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AK20 CCZ05788 578003.0 6452793.0 0 0.3 0.3 19.2 3.0 127.5 61.5 36.4 6.41 3.46 1.84 8.02 1.28 0.48 58.3 15.7 10.95 1.2 0.48 3.32 405.1 248.5 328.4 76.7 0.31 0.29 29.1
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AL12 CCZ05789 578197.0 6454400.0 0 0.3 0.3 14.4 2.0 84.5 42 31.5 5.59 3.19 1.43 6.39 1.17 0.45 38.5 10.2 7.81 0.96 0.47 3.08 285.5 181.7 219.3 66.1 0.33 0.28 28.4
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AL13 CCZ05790 578199.0 6454196.0 0 0.3 0.3 11.6 1.9 74.2 38 31.9 4.89 3.09 1.28 5.46 1.06 0.48 34.2 8.88 6.49 0.85 0.44 3.02 258.0 166.8 193.9 64.1 0.34 0.28 27.5
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AL14 CCZ05791 578199.0 6453998.0 0 0.3 0.3 12.6 2.1 86.3 42.5 33.8 5.73 3.48 1.34 6.02 1.22 0.49 39.9 10.65 7.84 0.99 0.49 3.53 294.0 188.0 224.4 69.7 0.34 0.28 28.3
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AL15 CCZ05792 578199.0 6453798.0 0 0.3 0.3 15.0 2.3 121.5 63.4 33.6 5.58 3.26 1.5 6.53 1.14 0.47 51.9 14.9 8.81 0.98 0.48 3.21 381.6 232.4 312.4 69.3 0.29 0.27 27.2
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AL16 CCZ05793 578200.0 6453600.0 0 0.3 0.3 13.2 2.7 107 55.9 33.4 5.83 3.31 1.46 7 1.19 0.47 47.4 13.1 8.9 1.03 0.48 3.22 348.4 217.0 278.4 70.0 0.31 0.28 28.0
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AL17 CCZ05794 578200.0 6453400.0 0 0.3 0.3 20.1 3.3 137.5 66.9 39.3 7.07 4.07 1.83 8.71 1.44 0.55 62 16.95 11.85 1.22 0.56 3.56 437.1 268.2 353.9 83.2 0.31 0.29 28.9
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AL18 CCZ05795 578198.0 6453200.0 0 0.3 0.3 21.6 3.5 130.5 62.6 44 7.35 4.67 1.63 8.11 1.51 0.72 57.9 15.4 10.75 1.22 0.69 4.59 423.2 262.9 332.3 90.9 0.32 0.28 27.8
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AL19 CCZ05796 578202.0 6452996.0 0 0.3 0.3 16.5 2.5 97.6 50.1 42.7 6.97 4.4 1.62 7.35 1.48 0.64 46.6 11.95 9.15 1.2 0.63 4.2 345.0 225.1 258.1 86.9 0.35 0.28 28.2
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AL20 CCZ05797 578206.0 6452796.0 0 0.3 0.3 18.4 3.4 125.5 59.4 33.7 5.89 3.37 1.42 6.8 1.18 0.52 51.5 14.1 9.62 1.03 0.52 3.39 382.6 228.4 312.1 70.5 0.29 0.27 27.2
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AM12 CCZ05798 578401.0 6454397.0 0 0.3 0.3 14.3 2.3 91.7 45.1 35 5.9 3.43 1.44 6.43 1.18 0.52 41.8 11.05 8 0.97 0.52 3.44 308.7 196.1 236.9 71.8 0.33 0.28 28.1
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AM13 CCZ05799 578398.0 6454195.0 0 0.3 0.3 13.4 1.9 74.9 37 28.8 4.96 2.98 1.35 5.42 1.01 0.42 34.4 9.21 7.06 0.86 0.43 3 254.9 162.9 194.8 60.0 0.33 0.28 28.4
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AM14 CCZ05800 578402.0 6453997.0 0 0.3 0.3 16.9 2.1 90.1 42.7 33.7 5.48 3.28 1.24 5.89 1.14 0.45 40.9 10.65 8.18 0.92 0.42 3.12 298.8 188.1 230.8 68.0 0.33 0.28 28.2
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AM15 CCZ05801 578400.0 6453800.0 0 0.3 0.3 13.7 2.3 117 57 41.3 6.92 4 1.44 7.23 1.43 0.55 47.7 12.9 9.4 1.15 0.58 3.99 376.5 232.8 292.7 83.8 0.32 0.26 26.5
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AM16 CCZ05802 578401.0 6453596.0 0 0.3 0.3 22.6 3.6 115 56.6 31.1 5.8 3.28 1.22 6.9 1.15 0.46 48.4 13.55 9.59 1.06 0.46 3.14 358.0 216.8 291.6 66.5 0.29 0.28 27.9
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AM17 CCZ05803 578402.0 6453395.0 0 0.3 0.3 12.3 2.6 82.5 40.1 29.7 5.05 2.97 1.19 5.54 1.1 0.47 36.3 9.76 7.47 0.84 0.46 2.98 272.5 171.2 211.2 61.4 0.32 0.28 27.9
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AM18 CCZ05804 578398.0 6453196.0 0 0.3 0.3 16.4 3.5 106 53.1 41.4 7.04 4.2 1.7 7.76 1.47 0.62 49.9 12.95 9.76 1.2 0.61 3.82 362.9 232.7 277.7 85.2 0.34 0.29 28.6
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AM19 CCZ05805 578400.0 6452994.0 0 0.3 0.3 14.9 3.1 96.6 48.1 34.7 5.77 3.49 1.35 6.24 1.21 0.5 43.3 11.25 8.36 1.02 0.53 3.3 319.8 201.2 248.9 71.0 0.33 0.28 27.8
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AM20 CCZ05806 578402.0 6452797.0 0 0.3 0.3 16.6 2.6 99.9 53 37.1 6 3.63 1.5 7.02 1.29 0.51 45 12.15 8.79 1.08 0.49 3.37 337.9 215.2 262.2 75.7 0.32 0.28 27.7
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AN12 CCZ05807 578598.0 6454396.0 0 0.3 0.3 13.9 2.2 76.5 37.8 36.7 5.74 3.64 1.16 6.03 1.27 0.59 35.5 9.45 7.17 0.95 0.56 3.72 273.2 179.2 199.4 73.8 0.36 0.28 27.7
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AN13 CCZ05808 578600.0 6454197.0 0 0.3 0.3 15.2 2.3 84.9 43 37.1 6.28 3.82 1.22 6.42 1.35 0.57 40.3 10.6 7.92 0.99 0.57 3.97 299.8 195.5 223.7 76.0 0.35 0.28 28.3
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AN14 CCZ05809 578600.0 6453994.0 0 0.3 0.3 16.9 3.0 113 58.1 51 8.69 5.24 1.28 8.76 1.82 0.75 53.6 14.2 10.2 1.36 0.78 5.27 402.2 263.4 298.5 103.7 0.35 0.28 28.1
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AN15 CCZ05810 578599.0 6453795.0 0 0.3 0.3 19.5 5.5 113.5 55.4 43.2 7.4 4.41 1.47 7.3 1.47 0.73 49 12.95 9.25 1.19 0.71 4.8 376.6 237.2 287.9 88.7 0.33 0.27 27.0
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AN16 CCZ05811 578599.0 6453597.0 0 0.3 0.3 13.3 2.8 100.5 49.8 31.7 5.53 3.12 1.32 6.13 1.08 0.52 44 11.85 8.22 0.95 0.45 3.34 323.1 199.6 257.0 66.0 0.31 0.28 27.8
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AN17 CCZ05812 578600.0 6453397.0 0 0.3 0.3 13.5 2.6 94 44.6 37.6 6.16 3.54 1.58 7.17 1.35 0.54 42.3 10.85 8.36 1.06 0.59 3.81 317.3 201.8 239.9 77.4 0.34 0.28 28.0
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AN18 CCZ05813 578603.0 6453197.0 0 0.3 0.3 14.2 2.4 87 42.6 34.8 5.73 3.57 1.2 6.32 1.22 0.54 39.2 10.35 7.64 0.99 0.54 3.42 295.1 188.3 223.9 71.2 0.34 0.28 27.8
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AN19 CCZ05814 578599.0 6452996.0 0 0.3 0.3 15.2 3.3 104 51.5 38.7 6.83 4.15 1.64 7.36 1.44 0.55 46.9 12.55 9.19 1.18 0.58 3.59 349.2 221.4 268.7 80.5 0.33 0.28 28.1
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AN20 CCZ05815 578600.0 6452794.0 0 0.3 0.3 16.9 3.0 99.3 50.4 38.9 6.37 4.14 1.46 7.01 1.42 0.57 46 12.35 8.75 1.14 0.62 3.75 339.6 217.6 259.8 79.8 0.33 0.28 28.1
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_V22 CCZ05816 574999.0 6452396.0 0 0.3 0.3 15.9 2.3 95.6 46.8 32.9 5.6 3.69 1.25 6.19 1.17 0.47 45.5 11.35 8.64 0.93 0.55 2.95 317.1 199.7 249.1 68.0 0.33 0.29 28.8
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_V24 CCZ05817 575004.0 6451998.0 0 0.3 0.3 19.3 2.8 104 50.8 30.7 5.76 3.46 1.34 6.99 1.15 0.44 47.8 12 9.51 1.04 0.42 2.64 334.3 206.5 268.6 65.7 0.31 0.29 29.1
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_V26 CCZ05818 575000.0 6451593.0 0 0.3 0.3 12.9 1.9 65.3 33.9 23.7 4.3 2.71 0.91 4.61 0.89 0.37 32.1 7.83 6.3 0.71 0.37 2.31 224.0 143.8 174.2 49.8 0.33 0.29 29.1
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_V28 CCZ05819 574997.0 6451196.0 0 0.3 0.3 14.2 2.2 77.7 39.1 32.1 5.26 3.59 1.14 5.92 1.16 0.53 38.6 9.68 7.32 0.89 0.55 3.13 272.7 177.3 206.5 66.2 0.35 0.29 29.0
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_V30 CCZ05820 575000.0 6450798.0 0 0.3 0.3 12.8 1.9 71.5 35.7 27.9 4.76 3.18 1.12 5.29 1.02 0.44 35 8.7 6.8 0.79 0.44 2.79 247.1 159.3 188.9 58.2 0.34 0.29 29.0
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_X22 CCZ05821 575400.0 6452404.0 0 0.3 0.3 14.9 2.4 99.5 46.8 28.5 5.07 3.07 1.56 6.69 1.03 0.38 46.6 11.7 9.41 0.93 0.4 2.41 317.5 195.2 256.5 60.9 0.31 0.30 29.6
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_X24 CCZ05822 575401.0 6452002.0 0 0.3 0.3 16.4 1.9 65.9 33.5 26 4.08 2.73 1.01 5.02 0.94 0.39 32.6 8 6.02 0.76 0.36 2.36 228.2 147.3 174.9 53.3 0.34 0.29 28.9
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_X26 CCZ05823 575398.0 6451601.0 0 0.3 0.3 15.6 2.6 112 50.7 35.2 6.31 4.16 1.68 7.48 1.37 0.53 51.2 13.2 9.88 1.11 0.59 3.22 359.3 221.7 284.2 75.1 0.32 0.29 29.0
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_X28 CCZ05824 575404.0 6451203.0 0 0.3 0.3 17.5 2.9 97.4 46.5 33.8 5.53 3.97 1.16 6.63 1.26 0.54 44 11.5 8.69 0.99 0.51 3.46 320.0 200.4 249.5 70.5 0.32 0.28 28.3
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_X30 CCZ05825 575398.0 6450803.0 0 0.3 0.3 15.4 2.4 77.4 37.5 31.4 5.02 3.39 1.04 5.51 1.06 0.45 36 9.23 6.81 0.87 0.48 2.88 263.7 168.7 200.1 63.6 0.34 0.28 28.1
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_Z22 CCZ05826 575800.0 6452401.0 0 0.3 0.3 17.0 2.8 101 48.3 30.1 5.37 3.15 1.25 6.53 1.14 0.43 45.6 11.75 9.2 0.97 0.43 2.76 322.3 198.2 258.8 63.5 0.31 0.29 28.8
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_Z24 CCZ05827 575803.0 6451997.0 0 0.3 0.3 14.6 2.3 100 48.8 29.9 5.33 3.53 1.5 6.65 1.12 0.42 47.2 12.35 9.19 0.94 0.44 2.64 324.6 201.8 260.7 63.9 0.31 0.29 29.4
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_Z26 CCZ05828 575798.0 6451599.0 0 0.3 0.3 17.2 2.8 100.5 47.7 36.9 6.12 4.45 1.28 6.65 1.38 0.59 46.4 11.75 8.64 1.03 0.57 3.63 334.1 210.6 257.7 76.4 0.33 0.28 28.2
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_Z28 CCZ05829 575801.0 6451202.0 0 0.3 0.3 15.7 2.4 91.7 45.4 34 5.77 3.97 1.2 6.48 1.2 0.5 45 11.25 8.5 0.97 0.51 3.35 312.5 199.9 241.8 70.7 0.34 0.29 29.2
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_Z30 CCZ05830 575802.0 6450799.0 0 0.3 0.3 15.3 2.4 80.9 41.4 33.2 5.66 3.83 1.3 6.33 1.24 0.49 40.3 10 7.73 0.98 0.51 3.41 285.4 186.0 216.0 69.4 0.34 0.29 29.1
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AB22 CCZ05831 576199.0 6452399.0 0 0.3 0.3 13.0 2.4 82.9 41.2 28 5 3.17 1.41 5.57 0.97 0.33 38.6 9.6 7.18 0.8 0.41 2.45 273.8 171.9 215.1 58.7 0.32 0.29 28.5
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AB24 CCZ05832 576198.0 6451999.0 0 0.3 0.3 18.0 3.1 108 50.8 34.6 6.03 3.64 1.4 6.95 1.2 0.51 48 12.2 9.16 1.07 0.49 3.33 345.8 213.1 273.6 72.2 0.32 0.28 28.2
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AB26 CCZ05833 576201.0 6451598.0 0 0.3 0.3 16.8 2.5 96.5 49.3 33.3 5.83 3.78 1.32 6.93 1.2 0.51 48.7 12.1 8.73 1 0.53 2.99 327.9 209.3 257.9 70.0 0.33 0.30 29.7
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AB28 CCZ05834 576201.0 6451197.0 0 0.3 0.3 15.6 2.6 106.5 50.7 32.6 5.7 3.71 1.51 6.67 1.18 0.43 49.6 12.35 9.57 1.03 0.49 2.94 342.7 211.9 274.2 68.6 0.32 0.29 29.0
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_AB30 CCZ05835 576201.0 6450798.0 0 0.3 0.3 12.4 1.9 66.5 32 29.4 4.62 3.41 1.12 5.22 1.02 0.39 33.1 7.8 6.39 0.86 0.46 2.71 234.7 153.1 174.7 60.1 0.36 0.29 28.9
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
FG_SM_POC CCZ05836 575129.0 6451468.0 0 0.3 0.3 18.0 2.9 103.5 52.2 36.1 5.57 4.15 1.5 7.31 1.28 0.6 49.9 12.8 9.52 1.06 0.61 3.64 348.4 221.3 273.1 75.4 0.33 0.29 28.9
========== ========= ========== ===== ==== ========== ===== ==== ====== ===== ===== ====== ===== ===== ====== ===== ===== ===== ====== ====== ===== ===== ===== ====== ======== ====== ====== ===== ===== =======
Notes:
1. Verification has been undertaken by CCZ Geology team personnel.
2. Sample results from ALS method ME-ICP81.
Source: ALS Adelaide.
APPIX D: JORC CODE, 2012 EDITION - TABLE 1 - FENCE GOSSAN
SURFACE SAMPLING
Section 1: Sampling Techniques and Data
Criteria JORC Code explanation Commentary
Sampling Nature and quality of Diamond Drilling (DDH)
techniques sampling (e.g., cut Diamond drilling of HQ diameter (TT_005DD)
channels, random was completed to 137.7m recently in the completed
chips, or specific program and was located 5m away from a RC hole
specialised already drilled (TT_003RC).
industry standard Reverse Circulation ('RC') Drilling
measurement tools RC drilling at Fence Gossan was used to obtain
appropriate a representative sample by means of riffle
to the minerals under splitting with samples submitted for analysis
investigation, such using the above-mentioned methodologies.
as Four (4) reverse circulation (RC) holes for
down hole gamma a total of 516m have been completed at the
sondes, or handheld Fence Gossan Prospect.
XRF instruments, Four (4) RC holes were completed at Reefs Tank
etc.). These examples for a total of 564m.
should not be taken At Tors Tank, four (4) RC holes for a total
as of 625.7m (including the cored hole) were completed.
limiting the broad The RC drilling technique was used to obtain
meaning of sampling. a representative sample by means of a cone
Include reference to or riffle splitter with samples submitted for
measures taken to assay by mixed acid digestion and analysis
ensure via ICP-MS + ICP-AES with anticipated reporting
sample representivity a suite of 48 elements (sulphur >10% by LECO)
and the appropriate Surface Sampling
calibration Two large surface sampling programs were conducted
of any measurement on grids based about the drilling at Tors Tank
tools or systems and Fence Gossan. The sampling was by using
used. hand auger to take soil samples from depth
Aspects of the varying between 0.1-0.5m. Original samples
determination of were between 0.5-2kg in weight, reduced to
mineralisation 200g for crushing and pulverizing. The Stage
that are Material to 1 program consisted of 189 sampling stations,
the Public Report. spaced at 200m intervals across a total survey
In cases where area measuring 6.4km(2)
'industry standard' The first area was based about the centre of
work has the grid, closest to the known points of observations
been done this would (drill holes FG001RC-4RC). Stations extended
be relatively simple east of the Resource Mask to the EL8434 lease
(e.g., boundary. Stations also extended west to identify
'reverse circulation extension of REEs into the Reef Tank Resource
drilling was used to Area. Station numbers are based on a wider
obtain grid that incorporates Reef Tank and Tors Tank.
1 m samples from A Stage 2 second area at a larger spacing (400m)
which 3 kg was was completed slighter later in December 2022,
pulverised which managed to collect another 21 samples
to produce a 30g over mainly pegmatite outcrop.
charge for fire
assay'). In
other cases, more
explanation may be
required,
such as where there
is coarse gold that
has
inherent sampling
problems. Unusual
commodities
or mineralisation
types (eg submarine
nodules)
may warrant
disclosure of
detailed information.
================================= =====================================================================================================
Drilling Drill type (e.g., Historical drilling consisted of auger, rotary
techniques core, reverse air blast, reverse circulation, and NQ, BQ,
circulation, and HQ diamond coring. One cored hole of HQ
open-hole hammer, (61mm) diameter was completed at Tors Tank
rotary air blast, after all the RC holes had been completed.
auger, Diamond drilling was completed with standard
Bangka, sonic, etc.) diameter, conventional HQ, with historical
and details (e.g., holes typically utilizing RC and percussion
core pre-collars to an average 30 metres (see drillhole
diameter, triple or information for further details).
standard tube, depth
of
diamond tails,
face-sampling bit or
other type,
whether core is
oriented and if so,
by what
method, etc.).
================================= =====================================================================================================
Drill sample Method of recording Reverse Circulation ('RC') Drilling - Reverse
recovery and assessing core circulation sample recoveries were visually
and estimated during drilling programs. Where the
chip sample estimated sample recovery was below 100% this
recoveries and was recorded in field logs by means of qualitative
results assessed. observation.
Measures taken to Reverse circulation drilling employed sufficient
maximise sample air (using a compressor and booster) to maximise
recovery sample recovery. Historical cored drillholes
and ensure by North Broken Hill, CRA , and Pasminco were
representative nature well documented and generally have >90% core
of the samples. recovery.
Whether a No relationship between sample recovery and
relationship exists grade has been observed.
between sample
recovery and grade
and whether sample
bias
may have occurred due
to preferential
loss/gain
of fine/coarse
material.
================================= =====================================================================================================
Logging Whether core and chip The drilling that did occur was completed to
samples have been modern-day standards. The preferred exploration
geologically strategy in the eighties and early nineties
and geotechnically was to drill shallow auger holes to negate
logged to a level of the influence of any Quaternary and Tertiary
detail sedimentary cover, and then return to sites
to support where anomalous Cu or Zn were assayed. In this
appropriate Mineral program at all three areas holes were completed
Resource estimation, to varying depths ranging from 100-160m.
mining studies and No downhole geophysical logging took place;
metallurgical however, measurements of magnetic susceptibility
studies. were taken at the same 1m intervals as the
Whether logging is PXRF readings were taken.
qualitative or
quantitative
in nature. Core (or
costean, channel,
etc)
photography.
The total length and
percentage of the
relevant
intersections logged.
================================= =====================================================================================================
Sub-sampling If core, whether cut Core samples will be hand-split or sawn with
techniques or sawn and whether re-logging of available historical core indicating
and sample quarter, a 70:30 (retained: assayed) split was typical.
preparation half or all core The variation of sample ratios noted are considered
taken. consistent with the sub-sampling technique
If non-core, whether (hand-splitting).
riffled, tube No second half samples will be submitted for
sampled, analysis, but duplicates have been taken at
rotary split, etc and a frequency of 1:20 in samples collected.
whether sampled wet It is considered water planned to be used for
or core cutting is unprocessed and unlikely to
dry. have introduced sample contamination.
For all sample types, Procedures relating to the definition of the
the nature, quality, line of cutting or splitting are not available.
and appropriateness It is expected that 'standard industry practice'
of the sample for the period was applied to maximize sample
preparation representivity.
technique. Quarter core will be submitted to ALS for chemical
Quality control analysis using industry standard sample preparation
procedures adopted and analytical techniques.
for all The sample interval details and grades quoted
sub-sampling stages for cored intervals described in various maps
to maximise in the main section are given in previous ASX
representivity releases (Castillo Copper 2022a, b, c, d, e,
of samples. f, g).
Measures taken to
ensure that the
sampling
is representative of
the in-situ material
collected,
including for
instance results for
field
duplicate/second-half
sampling.
Whether sample sizes
are appropriate to
the
grain size of the
material being
sampled.
================================= =====================================================================================================
Quality The nature, quality and The following rare earth elements were analysed
of assay appropriateness of using ME-MS61R Sample Decomposition is by
data and the assaying and laboratory HF-HNO(3) -HClO(4) acid digestion, HCl leach
laboratory procedures used (GEO-4A01). The Analytical Method for
tests and whether the technique Silver is shown below: Element Symbol Units Lower Upper
is considered partial Limit Limit
or total. Silver Ag ppm 0.01 100
For geophysical tools, ======== ======= ======= =======
spectrometers, handheld
XRF instruments, etc, the Inductively Coupled Plasma - Atomic Emission
parameters used in Spectroscopy (ICP - AES) Inductively Coupled
determining the analysis Plasma - Mass Spectrometry (ICP-MS)
including instrument A prepared sample (0.25 g) is digested with
make and model, reading perchloric, nitric, hydrofluoric, and hydrochloric
times, calibrations acids. The residue is topped up with dilute
factors applied and their hydrochloric acid and analysed by inductively
derivation, etc. coupled plasma atomic emission spectrometry.
Nature of quality control Following this analysis, the results are
procedures adopted reviewed for high concentrations of bismuth,
(eg standards, blanks, mercury, molybdenum, silver, and tungsten
duplicates, external and diluted accordingly.
laboratory checks) and Samples meeting this criterion are then analysed
whether acceptable levels by inductively coupled plasma-mass spectrometry.
of accuracy (i.e. lack of Results are corrected for spectral interelement
bias) and precision interferences.
have been established. Four acid digestions can dissolve most minerals:
however, although the term "near total" is
used, depending on the sample matrix, not
all elements are quantitatively extracted.
Results for the additional rare earth elements
will represent the acid leachable portion
of the rare earth elements and as such, cannot
be used, for instance to do a chondrite plot.
Geochemical Procedure
Element geochemical procedure reporting units
and limits are listed below: Element Symbol Units Lower Upper
Limit Limit
Aluminum Al % 0.01 50
======== ======= ======= ========
Arsenic As ppm 0.2 10 000
======== ======= ======= ========
Barium Ba ppm 10 10 000
======== ======= ======= ========
Beryllium Be ppm 0.05 1 000
======== ======= ======= ========
Bismuth Bi ppm 0.01 10 000
======== ======= ======= ========
Calcium Ca % 0.01 50
======== ======= ======= ========
Cadmium Cd ppm 0.02 1 000
======== ======= ======= ========
Cerium Ce ppm 0.01 500
======== ======= ======= ========
Cobalt Co ppm 0.1 10 000
======== ======= ======= ========
Chromium Cr ppm 1 10 000
======== ======= ======= ========
Cesium Cs ppm 0.05 500
======== ======= ======= ========
Copper Cu ppm 0.2 10 000
======== ======= ======= ========
Iron Fe % 0.01 50
======== ======= ======= ========
Gallium Ga ppm 0.05 10 000
======== ======= ======= ========
Germanium Ge ppm 0.05 500
======== ======= ======= ========
Hafnium Hf ppm 0.1 500
======== ======= ======= ========
Indium In ppm 0.005 500
======== ======= ======= ========
Potassium K % 0.01 10
======== ======= ======= ========
Lanthanum La ppm 0.5 10 000
======== ======= ======= ========
Lithium Li ppm 0.2 10 000
======== ======= ======= ========
Magnesium Mg % 0.01 50
======== ======= ======= ========
Manganese Mn ppm 5 100 000
======== ======= ======= ========
Element Symbol Units Lower Upper Limit
Limit
Molybdenum Mo ppm 0.05 10 000
======== ======= ======= ============
Sodium Na % 0.01 10
======== ======= ======= ============
Niobium Nb ppm 0.1 500
======== ======= ======= ============
Nickel Ni ppm 0.2 10 000
======== ======= ======= ============
Phosphorous P ppm 10 10 000
======== ======= ======= ============
Lead Pb ppm 0.5 10 000
======== ======= ======= ============
Rubidium Rb ppm 0.1 10 000
======== ======= ======= ============
Rhenium Re ppm 0.002 50
======== ======= ======= ============
Sulphur S % 0.01 10
======== ======= ======= ============
Antimony Sb ppm 0.05 10 000
======== ======= ======= ============
Scandium Sc ppm 0.1 10 000
======== ======= ======= ============
Selenium Se ppm 1 1 000
======== ======= ======= ============
Tin Sn ppm 0.2 500
======== ======= ======= ============
Strontium Sr ppm 0.2 10 000
======== ======= ======= ============
Tantalum Ta ppm 0.05 100
======== ======= ======= ============
Tellurium Te ppm 0.05 500
======== ======= ======= ============
Thorium Th ppm 0.2 10 000
======== ======= ======= ============
Titanium Ti % 0.005 10
======== ======= ======= ============
Thallium Tl ppm 0.02 10 000
======== ======= ======= ============
Uranium U ppm 0.1 10 000
======== ======= ======= ============
Vanadium V ppm 1 10 000
======== ======= ======= ============
Tungsten W ppm 0.1 10 000
======== ======= ======= ============
Method ME-MS81
This method involves a lithium borate fusion
prior to acid dissolution and ICP- MS analysis
provides the most quantitative analytical
approach for a broad suite of trace elements.
Options for adding the whole rock elements
from an |CP - AES analysis on the same fusion,
or base metals from a separate four acid
digestion, are available.
Lower and upper detection limits are given
below: Element Symbol Units Lower Upper
Limit Limit
Yttrium Y ppm 0.1 500
======== ======= ======= =======
Zinc Zn ppm 2 10 000
======== ======= ======= =======
Zirconium Zr ppm 0.5 500
======== ======= ======= =======
Dysprosium Dy ppm 0.05 1 000
======== ======= ======= =======
Erbium Er ppm 0.03 1 000
======== ======= ======= =======
Europium Eu ppm 0.03 1 000
======== ======= ======= =======
Gadolinium Gd ppm 0.05 1 000
======== ======= ======= =======
Holmium Ho ppm 0.01 1 000
======== ======= ======= =======
Lutetium Lu ppm 0.01 1 000
======== ======= ======= =======
Neodymium Nd ppm 0.1 1 000
======== ======= ======= =======
Praseodymium Pr ppm 0.03 1 000
======== ======= ======= =======
Samarium Sm ppm 0.03 1 000
======== ======= ======= =======
Terbium Tb ppm 0.01 1 000
======== ======= ======= =======
Thulium Tm ppm 0.01 1 000
======== ======= ======= =======
Ytterbium Yb ppm 0.03 1 000
======== ======= ======= =======
* Laboratory inserted standards, blanks and duplicates
were analysed per industry standard practice. There
was no evidence of bias from these results.
================================= =====================================================================================================
Verification The verification of
of sampling significant * Two of the drillholes have been twinned, at Tors Tank
and assaying intersections where TT_005DD was drilled next to TT_003RC.
by either independent
or alternative
company * Conversion of elemental analysis (REE parts per
personnel. million) to stoichiometric oxide (REO parts per
The use of twinned million) was undertaken by ROM geological staff using
holes. the below element to stoichiometric oxide conversion
Documentation of factors (
primary data, data https://www.jcu.edu.au/news/releases/2020/march/rare-earth-metals-an-untapped-resource
entry )
procedures, data
verification, data
storage
(physical and Table C1-1: Element -Conversion Factor -Oxide
electronic) Form
protocols. Ce 1.2284 CeO(2)
Discuss any ============== ===================
adjustment to assay Dy 1.1477 Dy(2) O(3)
data. ============== ===================
Er 1.1435 Er(2) O(3)
============== ===================
Eu 1.1579 Eu(2) O(3)
============== ===================
Gd 1.1526 Gd(2) O(3)
============== ===================
Ho 1.1455 Ho(2) O(3)
============== ===================
La 1.1728 La(2) O(3)
============== ===================
Lu 1.1371 Lu(2) O(3)
============== ===================
Nd 1.1664 Nd(2) O(3)
============== ===================
Pr 1.2083 Pr(6) O(11)
============== ===================
Sm 1.1596 Sm(2) O(3)
============== ===================
Tb 1.1762 Tb(4) O(7)
============== ===================
Tm 1.1421 Tm(2) O(3)
============== ===================
Y 1.2699 Y(2) O(3)
============== ===================
Yb 1.1387 Yb(2) O(3)
============== ===================
Rare earth oxide is the industry accepted form
for reporting rare earths. The following calculations
are used for compiling REO into their reporting
and evaluation groups:
TREO (Total Rare Earth Oxide) = La(2) O(3)
+ CeO(2) + Pr(6) O(11) + Nd(2) O(3) + Sm(2)
O(3) + Eu(2) O(3) + Gd(2) O(3) + Tb(4) O(7)
+ Dy(2) O(3) + Ho(2) O(3) + Er(2) O(3) + Tm(2)
O(3) + Yb(2) O(3) + Y(2) O(3) + Lu(2) O(3)
.
TREO-Ce = TREO - CeO(2)
LREO (Light Rare Earth Oxide) = La(2) O(3)
+ CeO(2) + Pr(6) O(11) + Nd(2) O(3) + Sm(2)
O(3)
HREO (Heavy Rare Earth Oxide) = Eu(2) O(3)
+ Gd(2) O(3) + Tb(4) O(7) + Dy(2) O(3) + Ho(2)
O(3) + Er(2) O(3) + Tm2O3 + Yb2O3 + Y2O3 +
Lu2O3
CREO (Critical Rare Earth Oxide) = Nd(2) O(3)
+ Eu(2) O(3) + Tb(4) O(7) + Dy(2) O(3) + Y(2)
O(3)
MREO (Magnetic Rare Earth Oxide) = Pr(6) O(11)
+ Nd(2) O(3) + Sm(2) O(3) + Gd(2) O(3) + Tb(4)
O(7) + Dy(2) O(3) .
Total Rare Earth Oxides (TREO):
To calculate TREO an oxide conversion "factor"
is applied to each rare-earth element assay.
The "factor" equates an elemental assay to
an oxide concentration for each element. Below
is an example of the factor calculation for
Lanthanum (La):
o Relative Atomic Mass (La) = 138.9055
o Relative Atomic Mass (O) = 15.9994
o Oxide Formula = La(2) O(3)
o Oxide Conversion Factor = 1/ ((2x 138.9055)/(2x
138.9055 + 3x 15.9994)) Oxide Conversion Factor
= 1.173 (3dp)
None of the historical data has been adjusted.
================================= =====================================================================================================
Location Accuracy and quality In general, locational accuracy does vary,
of data of surveys used to depending upon whether the historical surface
points locate and drillhole samples were digitised off plans
drill holes (collar or had their coordinated tabulated. Many samples
and down-hole were originally reported to AGD66 or AMG84
surveys), and have been converted to MGA94 (Zone 54)
trenches, mine The holes are currently surveyed with handheld
workings and other GPS, awaiting more accurate DGPS survey. It
locations is thus estimated that locational accuracy
used in Mineral therefore varies between 2-4m until the more
Resource estimation. accurate surveying is completed. This assessment
Specification of the was confirmed once the holes were surveyed
grid system used. by DGPS from GMC Surveying.
Quality and adequacy The quality of topographic control (GSNSW 1
of topographic sec DEM) is deemed adequate for the purposes
control. of the exploration drilling program.
================================= =====================================================================================================
Data spacing Data spacing for The average sample spacing from the current
and reporting of drilling program across the tenure varies per
distribution Exploration prospect, and sample type, as listed in Table
Results. C1-2, below:
Whether the data Table C1-2: EL 8434 Drillhole Spacing Prospect Drillholes RMS Drillhole
spacing and Completed Spacing
distribution (m)
is sufficient to The Sisters Not yet
establish the degree =========== ==============
of geological Iron Blow Not Yet
and grade continuity =========== ==============
appropriate for the Tors Tank 4 127
Mineral =========== ==============
Resource and Ore Fence Gossan 4 208
Reserve estimation =========== ==============
procedure(s) Ziggy's n/a n/a
and classifications Hill
applied. =========== ==============
Whether sample Reefs Tank 4 221
compositing has been =========== ==============
applied.
The Datamine software allows creation of fixed
length samples from the original database given
a set of stringent rules.
Sample location is shown in Figure C1.
Figure C1: Location of Stage 1 Fence Gossan
Surface Samples
================================= =====================================================================================================
Orientation Whether the Historical drill holes at the BHAE are typically
of data orientation of drilled vertically for auger and RAB types
in relation sampling achieves (drilled along section lines) and angled at
to unbiased sampling of -55Ëš or -60Ëš to the horizontal and
geological possible structures drilled perpendicular to the mineralised trend
structure and for RC and DDH.
the extent to which Drilling orientations are adjusted along strike
this is known, to accommodate folded geological sequences.
considering All Fence Gossan holes were designed to drill
the deposit type. toward grid south at an inclination of 60 degrees
If the relationship from horizontal.
between the drilling The drilling orientation is not considered
orientation to have introduced a sampling bias on assessment
and the orientation of the current geological interpretation.
of key mineralised Geological mapping by various companies has
structures reinforced that the strata dips variously between
is considered to have 5 and 65 degrees.
introduced a sampling
bias, this should be
assessed and reported
if material.
================================= =====================================================================================================
Sample The measures taken to Sample security procedures are considered 'industry
security ensure sample standard' for the current period.
security. Samples obtained during drilling completed
between 4/10/22 to the 10/10/22 were transported
by exploration employees or an independent
courier directly from Broken Hill to ALS Laboratory,
Adelaide.
The Company considers that risks associated
with sample security are limited given the
nature of the targeted mineralisation.
================================= =====================================================================================================
Audits The results of any No external audits or reviews have yet been
or reviews audits or reviews of undertaken.
sampling
techniques and data.
================================= =====================================================================================================
SECTION 2: REPORTING OF EXPLORATION RESULTS
Criteria JORC Code explanation Commentary
Mineral Type, reference EL 8434 is located about 28km east of Broken
tenement name/number, Hill whilst EL 8435 is 16km east of Broken
and land location and Hill. Both tenures are approximately 900km
tenure status ownership northwest of Sydney in far western New South
including Wales (Figures C2-1 and C2-2 in Appendix A
agreements or &B, above).
material EL 8434 and EL 8435 were both granted on the
issues with 2(nd of) June 2016 to Squadron Resources for
third parties a term of five (5) years for Group One Minerals.
such as joint On the 25(th of) May 2020, Squadron Resources
ventures, changed its name to Wyloo Metals Pty Ltd (Wyloo).
partnerships, In December 2020 the tenure was transferred
overriding from Wyloo Metals to Broken Hill Alliance Pty
royalties, Ltd a 100% subsidiary company of Castillo Copper
native Limited. Both tenures were renewed on the 12(th
title interests, of) August 2021 for a further six (6) years
historical and are due to expire on the 2(nd of) June
sites, 2027.
wilderness EL 8434 lies across two (2) 1:100,000 geology
or national park map sheets Redan 7233 and Taltingan 7234, and
and two (2) 1:250,000 geology map sheets, SI54-3
environmental Menindee, and SH54-15 Broken Hill in the county
settings. of Yancowinna. EL 8434 consists of one hundred
The security of and eighty-six (186) units) in the Adelaide
the tenure held and Broken Hill 1:1,000,000 Blocks covering
at the time an area of approximately 580km(2) .
of reporting EL 8435 is located on the 1:100,000 geology
along with any map sheet Taltingan 7234, and the 1:250,000
known geology map sheet SH/54-15 Broken Hill in the
impediments county of Yancowinna. EL 8435 consists of twenty-two
to obtaining a (22) units (Table 1) in the Broken Hill 1:1,000,000
licence to Blocks covering an area of approximately 68km(2)
operate in the .
area. Access to the tenures from Broken Hill is via
the sealed Barrier Highway. This road runs
north-east to south-west through the northern
portion of the EL 8434, passes the southern
tip of EL 8435 eastern section and through
the middle of the western section of EL 8435.
Access is also available via the Menindee Road
which runs north-west to south-east through
the southern section of the EL 8434. The Orange
to Broken Hill Rail line also dissects EL 8435
western section the middle and then travels
north-west to south-east slicing through the
eastern arm of EL 8434 (Figure C2-1).
Figure C2-1: EL 8434 and EL 8435 General Location
Map
============================ =================================================================
Exploration Acknowledgment Explorers who were actively involved over longer
done by other and appraisal of historical periods in various parts of EL8434
parties exploration were: - North Broken Hill Ltd, CRAE Exploration,
by other Major Mining Ltd and Broken Hill Metals NL,
parties. Pasminco Exploration Ltd, Normandy Exploration
Ltd, PlatSearch NL/Inco Ltd/ EGC Pty Ltd JV
and the Western Plains Gold Ltd/PlatSearch/EGC
Pty Ltd JV.
A comprehensive summary of work by previous
explorers was presented in Leyh (2009). However,
more recently, follow-up field reconnaissance
of areas of geological interest, including
most of the prospective zones was carried out
by EGC Pty Ltd over the various licenses. This
work, in conjunction with a detailed interpretation
of aeromagnetic, gravity plus RAB / RC drill
hole logging originally led to the identification
of at least sixteen higher priority prospect
areas. All these prospects were summarized
in considerable detail in Leyh (2008). Future
work programs were then also proposed for each
area. Since then, further compilation work
plus detailed geological reconnaissance mapping
and sampling of gossans and lode rocks has
been carried out.
A total of 22 prospects were then recognised
on the exploration licence with at least 12
occurring in and around the tenure.
With less than 45% outcropping Proterozoic
terrain within the licence, this makes it very
difficult to explore and is in the main very
effectively screened from the easy application
of more conventional exploration methodologies
due to a predominance of extensive Cainozoic
cover sequences. These include recent to young
Quaternary soils, sands, clays and older more
resistant, only partially dissected, Tertiary
duricrust regolith covered areas. Depth of
cover ranges from a few metres in the north
to over 60 metres in some areas on the southern
and central license.
Exploration by EGC Pty Ltd carried out in the
field in the first instance has therefore been
heavily reliant upon time consuming systematic
geological reconnaissance mapping and relatable
geochemical sampling. These involve a slow
systematic search over low outcropping areas,
poorly exposed subcrops and float areas as
well as the progressive development of effective
regolith mapping and sampling tools. This work
has been combined with a vast amount of intermittently
acquired past exploration data. The recent
data compilation includes an insufficiently
detailed NSWGS regional mapping scale given
the problems involved, plus some regionally
extensive, highly variable, low-level stream
and soil BLEG geochemical data sets over much
of the area.
There are also a few useful local detailed
mapping grids at the higher priority prospects,
and many more numerous widespread regional
augers, RAB, and percussion grid drilling data
sets. Geophysical data sets including ground
magnetics, IP and EM over some prospect areas
have also been integrated into the exploration
models. These are located mainly in former
areas of moderate interest and most of the
electrical survey methods to date in this type
of terrain continue to be of limited application
due to the high degree of weathering and the
often prevailing and complex regolith cover
constraints.
Between 2007 and 2014 Eaglehawk Geological
Consulting has carried out detailed research,
plus compilation and interpretation of a very
large volume of historic exploration data sourced
from numerous previous explorers and dating
back to the early 1970's. Most of this data
is in non-digital scanned form. Many hard copy
exploration reports (see references) plus several
hundred plans have been acquired from various
sources, hard copy printed as well as downloaded
as scans from the Geological Survey of NSW
DIGS system. They also conducted field mapping,
costean mapping and sampling, and rock chip
sampling and analysis.
Work Carried out by Squadron Resources and
Whyloo Metals 2016-2020
Research during Year 1 by Squadron Resources
revealed that the PGE-rich, sulphide-bearing
ultramafic rocks in the Broken Hill region
have a demonstrably alkaline affinity. This
indicates a poor prospectivity for economic
accumulations of sulphide on an empirical basis
(e.g., in comparison to all known economic
magmatic nickel sulphide deposits, which have
a dominantly tholeiitic affinity). Squadron
instead directed efforts toward detecting new
Broken Hill-Type (BHT) deposits that are synchronous
with basin formation. Supporting this modified
exploration rationale are the EL's stratigraphic
position, proximity to the Broken Hill line
of lode, abundant mapped alteration (e.g.,
gahnite and/or garnet bearing exhalative units)
and known occurrences such as the "Sisters"
and "Iron Blow" prospects.
The area overlies a potential magmatic Ni-Cu-PGE
source region of metasomatised sub-continental
lithospheric mantle (SCLM) identified from
a regional targeting geophysical data base.
The exploration model at the time proposed
involved remobilization of Ni-Cu-PGE in SCLM
and incorporation into low degree mafic-ultramafic
partial melts during a post-Paleoproterozoic
plume event and emplacement higher in the crust
as chonoliths/small intrusives - Voisey's Bay
type model. Programs were devised to use geophysics
and geological mapping to locate secondary
structures likely to control and localise emplacement
of Ni-Cu-PGE bearing chonoliths. Since EL8434
was granted, the following has been completed:
* Airborne EM survey.
* Soil and chip sampling.
* Data compilation.
* Geological and logistical reconnaissance.
* Community consultations; and
* Execution of land access agreements.
Airborne EM Survey
Geotech Airborne Limited was engaged to conduct
an airborne EM survey using their proprietary
VTEM system in 2017. A total of 648.92-line
kilometres were flown on a nominal 200m line
spacing over a portion of the project area.
Several areas were infilled to 100m line spacing.
The VTEM data was interpreted by Southern Geoscience
Consultants Pty Ltd, who identified a series
of anomalies, which were classified as high
or low priority based on anomaly strength (i.e.,
does the anomaly persist into the latest channels).
Additionally, a cluster of VTEM anomalies at
the "Sisters" prospect have been classified
separate due to strong IP effects observed
in the data. Geotech Airborne have provided
an IP corrected data and interpretation of
the data has since been undertaken.
Soil and Chip sampling
The VTEM anomalies were followed up by a reconnaissance
soil sampling programme. Spatially clustered
VTEM anomalies were grouped, and follow-up
soil lines were designed. Two (2) VTEM anomalies
were found to be related to culture and consequently
no soils were collected. Two (2) other anomalies
were sampled which were located above thick
alluvium of Stephens Creek and were therefore
not sampled. A line of soil samples was collected
over a relatively undisturbed section at Iron
Blow workings and the Sisters Prospect.
One hundred and sixty-six (166) soil samples
were collected at a nominal 20cm depth using
a 2mm aluminum sieve. Two (2) rock chips were
also collected during this program. The samples
were collected at either 20m or 40m spacing
over selected VTEM anomalies. The samples were
pulverised and analysed by portal XRF at ALS
laboratories in Perth.
Each site was annotated with a "Regolith Regime"
such that samples from a depositional environment
could be distinguished from those on exposed
Proterozoic bedrock, which were classified
as an erosional environment. The Regolith Regime
groups were used for statistical analysis and
levelling of the results. The levelled data
reveals strong relative anomalies in zinc at
VTEM anomaly clusters 10, 12 and 14 plus strong
anomalous copper at VTEM 17.
============================ =================================================================
Geology Deposit type, As the strata is tightly folded, the intersected
geological cobalt-rich layers are overstated in terms
setting, and of apparent thickness, however the modelling
style software calculates a true, vertical thickness.
of Cobalt mineralisation is commonly associated
mineralisation. with shears, faults, amphibolites, and a
quartz-magnetite
rock within the shears, or on or adjacent to
the boundaries of the Himalaya Formation. In
general, most of the cobalt and rare earth
element - rich layers have a north-northwest
to north strike.
REE enrichment generally occurs as a 5 to
10-metre-thick
zone between the completely weathered layer
and strongly weathered layer and it is targeted
for commercial mining (Figure D2-2). Compared
to other REE deposits, regolith-hosted rare
earth element deposits are substantially low-moderate
grade (containing 0.05-0.3 wt.% extractable
REEs). Nevertheless, due to its easy extraction
method, low processing costs and large abundance,
the orebodies are generally economic to be
extracted ( Duuring, (2020); Kanazawa and Kamitani
(2006); and Murakami, H.; Ishihara (2008) ).
Figure C2-2: Weathering Profile over REE -
Rich Granite
https://en.wikipedia.org/wiki/Regolith-hosted_rare_ea
rth_element_deposits
Weathering profile of regolith hosted REE deposits
shown above, the legend is: (A) Humic layer.
(B) Completely weathered layer. (C) Strongly
weathered layer. (D) Weathering front. (E)
Unweathered rock.
Most of the REE found in cerium monazite (Ce
(PO(4) )) which always contains major to minor
amounts of other REE (Nd, La, Pr, Sm etc) replacing
Ce. Also, the mineral often contains trace
amounts of U and Th (coupled with Ca). This
will be collaborated with XRD and or SEM analysis.
============================ =================================================================
Drill hole A summary of all Header information about all drillholes and
Information information surface samples completed at Tors Tank and
material to Fence Gossan have been tabulated in this release
the in Appendix B.
understanding of
the exploration
results
including a
tabulation of
the following
information
for all Material
drill holes:
o easting and
northing of the
drill hole
collar
o elevation or
RL (Reduced
Level -
elevation
above sea level
in metres) of
the drill hole
collar
o dip and
azimuth of the
hole
o down hole
length and
interception
depth
o hole length.
If the exclusion
of this
information is
justified on the
basis that the
information
is not Material
and this
exclusion does
not
detract from the
understanding of
the report,
the Competent
Person should
clearly explain
why this is the
case.
============================ =================================================================
Data aggregation In reporting No metal equivalents have been reported. Rare
methods Exploration earth element results have been converted to
Results, rare earth oxides as per standard industry
weighting practice (Castillo Copper 2022f).
averaging No compositing of assay results has taken place,
techniques, but rather menu options within the Datamine
maximum and/or GDB module have been used to create fixed length
minimum 1m assay intervals from the original sampling
grade lengths.
truncations The rules follow very similarly to those used
(e.g., cutting by the Leapfrog Geo software in creating fixed
of high length samples.
grades) and
cut-off grades
are usually
Material
and should be
stated.
Where aggregate
intercepts
incorporate
short
lengths of
high-grade
results and
longer
lengths of
low-grade
results, the
procedure
used for such
aggregation
should be stated
and some typical
examples of such
aggregations
should be shown
in detail.
The assumptions
used for any
reporting of
metal equivalent
values should be
clearly
stated.
============================ =================================================================
Relationship These A database of all the historical borehole sampling
between relationships has been compiled and validated. It is uncertain
mineralisation are particularly if there is a strong relationship between the
widths and important surface sample anomalies to any subsurface
intercept in the reporting anomalous intersections due to the possible
lengths of Exploration masking by variable Quaternary and Tertiary
Results. overburden that varies in depth from 0-15m.
If the geometry The mineralisation appears to be secondary
of the enrichment in the regolith clays and extremely
mineralisation weathered material derived from quartzo-feldspathic
with pegmatites.
respect to the
drill hole angle
is known,
its nature
should be
reported.
If it is not
known and only
the down hole
lengths are
reported, there
should be a
clear
statement to
this effect
(e.g., 'down
hole
length, true
width not
known').
============================ =================================================================
Diagrams Appropriate maps Current surface anomalies are shown on maps
and sections released on the ASX (Castillo Copper 2022d,
(with scales) 2022e, 2022f and 2022g). All historical surface
and tabulations sampling has had their coordinates converted
of intercepts to MGA94, Zone 54.
should be
included
for any
significant
discovery being
reported
These should
include, but not
be limited
to a plan view
of drill hole
collar locations
and appropriate
sectional views.
============================ =================================================================
Balanced Where All recent laboratory analytical results have
reporting comprehensive been recently reported (see Castillo Copper
reporting of all 2022a, b, c, d, e, f, and g) for assay results.
Exploration Regarding the surface and sampling, no results
Results is not other than duplicates, blanks or reference
practicable, standard assays have been omitted.
representative
reporting of
both low and
high grades
and/or
widths should be
practiced to
avoid misleading
reporting of
Exploration
Results.
============================ =================================================================
Other substantive Other Historical explorers have also conducted airborne
exploration exploration and ground gravity, magnetic, EM, and IP resistivity
data data, if surveys over parts of the tenure area but this
meaningful and is yet to be fully georeferenced (especially
material, should the ground IP surveys). Squadron Resources
be reported conducted an airborne EM survey in 2017 that
including (but covers Iron Blow and The Sisters, but not the
not limited to): southern cobalt and REE prospects.
geological
observations;
geophysical
survey results;
geochemical
survey
results; bulk
samples - size
and method of
treatment;
metallurgical
test results;
bulk
density,
groundwater,
geotechnical and
rock
characteristics;
potential
deleterious or
contaminating
substances.
============================ =================================================================
Further The nature and It is recommended that:
work scale of planned * Complete rehabilitation of the 2022 BHAE drilling
further campaign that comprised mostly RC drilling. An
work (e.g., application supporting an ESF2 lodgment is yet to be
tests for approved by the NSW Resource Regulator
lateral
extensions
or depth * The remaining non-sampled zones within the Core
extensions or Library drillholes, BH1, BH2, and DD90-IB3 in the
large-scale north of the tenure group be relogged and sampled.
step-out DD90-IB3 had 21-87m retested recently and is a good
drilling). candidate for hyperspectral logging.
Diagrams clearly
highlighting the
areas * A program of field mapping and ground magnetic, IP or
of possible radiometric surveys be planned and executed at Fence
extensions, Gossan. Mapping of pegmatite outcrops is a high
including the priority.
main
geological
interpretations * Generate an Exploration Target for Fence Gossan to
and future the standard of Clause 17 of the 2012 JORC Code.
drilling
areas, provided
this information * Depending upon the results of the proposed
is not geophysical surveys and Exploration Target noted
commercially above, the next drilling program will specifically
sensitive. target the air coring technique over the known cobalt
and REE mineralisation downdip to at least 30m depth
at all three prospects. That proposed drilling
program is also designed to increase the resource
confidence of the REE to Inferred Resources to the
standard of the 2012 JORC Code.
============================ =================================================================
REFERENCES
Biggs, M. S., 2021a, Broken Hill Alliance, NSW Tenure Package
Background Geological Information, unpublished report to BH
Alliance Pty Ltd, Sep 21, 30pp.
Biggs, M. S., 2021b, EL 8434 and EL 8435, Brief Review of
Surface Sample Anomalies Lithium, Rare Earth Elements and Cobalt,
unpublished report to BH Alliance Pty Ltd, Nov 21, 18pp.
Biggs, M.S., 2022a, BHA Cobalt Modelling and Mineral Resource
Estimate Update, unpublished memo for Castillo Copper by ROM
Resources.
Biggs, M.S., 2022b, Broken Hill BHA Tenures Update, Castillo
Copper, unpublished memo prepared by ROM Resources, Mar 22,
5pp.
Biggs M.S., 2022c, Geological Briefing Paper, Iron Blow
Prospect, East Zone, BHA Project (BHAE), Broken Hill, NSW, ROM
Resources, prepared for Castillo Copper Limited, August 2022
Burkett R.D., 1975, Progress Report on Exploration Licenses 780,
781, 782 and 783, Broken Hill Area, NSW for the six months to 23rd
November 1975, North Broken Hill Limited for the NSW Geological
Survey, (GS1975-328)
Castillo Copper Limited, 2020, ASX Release Acquisition enhances
BHT (zinc-silver-lead) and IOCG (gold-copper) prospectivity at
Broken Hill, 1st October 2020.
Castillo Copper Limited, 2022a, ASX Release Battery metal
drill-hole assays unlock BHA East Zone potential / lithium update,
5th January 2022.
Castillo Copper Limited, 2022b, ASX Release Strategic focus to
develop significant cobalt mineralisation potential at BHA Project,
9th February 2022.
Castillo Copper Limited, 2022c, ASX Release High grade platinum
confirmed at BHA Project, 9th March 2022.
Castillo Copper Limited, 2022d ASX Release Diamond core tests
demonstrate high-grade cobalt-zinc potential at Broken Hill, 21
March 2022
Castillo Copper Limited, 2022e ASX Release, Drilling hits
targeted cobalt zones & wide pegmatite intercepts at Broken
Hill 12 October 2022
Castillo Copper Limited, 2022f ASX Release, Drilling hits more
wide pegmatite intercepts at Broken Hill, 24 October 2022
Castillo Copper Limited, 2022g ASX Release, Completed auger
sampling campaign targets 6.5km(2) REE mineralisation zone, 23
December 2022
Duuring, P 2020, Rare-element pegmatites: a mineral systems
analysis: Geological Survey of Western Australia, Record 2020/7,
6p.
Kanazawa, Y.; Kamitani, M., 2006, "Rare earth minerals and
resources in the world". Journal of Alloys and Compounds. 408:
1339-1343. doi:10.1016/j.jallcom.2005.04.033
Lees, T.C., 1978, Progress Report on Farmcote Exploration
Licenses 780 and 782, Farmcote Area, Broken Hill, NSW for the six
months to 23RD November 1978, North Broken Hill Limited for the NSW
Geological Survey, (GS1978-043)
Leyh, W.R., 1976, Progress Report on Exploration Licence, No.
846 Iron Blow -Yellowstone Area, Broken Hill, New South Wales for
the six months period ended 29th June 1976, North Broken Hill
Limited, Report GS1976-198, Jul 76, 88pp.
Leyh, W.R., 1977a, Progress Report on Exploration Licence, No.
846 Iron Blow -Yellowstone Area, Broken Hill, New South Wales for
the six months period ended 29th December 1976, North Broken Hill
Limited, Report GS1976-198, Feb 1977, 24pp.
Leyh W.R., 1977b, Progress Report on Farmcote Exploration
Licenses 780 and 782, Farmcote Area, Broken Hill, NSW for the three
months to 5th March 1977, North Broken Hill Limited for the NSW
Geological Survey, (GS1977-078)
Leyh W.R., 1977c, Progress Report on Farmcote Exploration
Licenses 780 and 782, Farmcote Area, Broken Hill, NSW for the three
months to 23rd May 1977, North Broken Hill Limited for the NSW
Geological Survey, (GS1977-078)
Leyh W.R., 1978, Progress Report on Farmcote Exploration
Licenses 780 and 782, Farmcote Area, Broken Hill, NSW for the three
months to 27 October 1978, North Broken Hill Limited for the NSW
Geological Survey, (GS1977-078)
Leyh W.R., 1978 Progress Report on Exploration Licenses 1099 and
1100 for the six months to 27 October 1978, North Broken Hill
Limited for the NSW Geological Survey, (GS1978-407).
Leyh, W.R., 1990, Exploration Report for the Third Six Monthly
Period ended 12th June 1990 for EL 3238 (K Tank), Broken Hill
District, New South Wales for the six months period, Pasminco
Limited, Report GS1989-226, Jun 90, 22pp.
Leyh, W.R., and Lees T.C., 1977, Progress Report on Exploration
Licence, No. 846 Iron Blow -Yellowstone Area, Broken Hill, New
South Wales for the six months period ended 29th June 1977, North
Broken Hill Limited, Report GS1976-198, Jul 77, 35pp.
Leyh, W.R., and Larson P.D., 1981, Final Report for the Third
Six Monthly Period ended 12th June 1990 for EL 3238 (K Tank),
Broken Hill District, New South Wales for the six months period,
Pasminco Limited, Report GS1989-226, Jun 90, 22pp.
McConachie, G.W., 1997, EL 4792 Redan, Annual Report for the
period ending 19/2/1997, Normandy Exploration Limited, unpublished
report to the GSNSW, RIN 00002672
Main, J.V., and Tucker D.F., 1981, Exploration Report for Six
Month Period 8th November 1980 to 7th May 1981, EL 1106 Rockwell,
Broken Hill, NSW, CRA Exploration Pty Ltd, GS1980-080, Jul 1981,
40pp
Mohoney, M., 2018, BHA Broken Hill Project Position Paper,
Squadron Resources Pty Ltd., Unpublished report, Mar2018, 8pp.
Mortimer R., 2017, Re-interpretation of VTEM Profiles Broken
Hill Area, unpublished report by Southern Geoscience Consultants
for Squadron Resources Pty Ltd, Oct 17.
https://en.wikipedia.org/wiki/Regolith-hosted_rare_earth_element_deposits
Murakami, H.; Ishihara, S., 2008, REE mineralization of
weathered crust and clay sediment on granitic rocks in the Sanyo
Belt, SW Japan and the Southern Jiangxi Province, China". Resource
Geology. 58 (4): 373-401. doi:10.1111/j.1751-3928.2008.00071.x.
Segnit, E.R. (1946) Barium-feldspars from Broken Hill, New South
Wales. Mineralogical Magazine, 27, 166-174.
Squadron Resources Pty Ltd, 2018, Broken Hill Project Status,
August 2018, unpublished confidential presentation by Squadron
Resources,
Timms, P.D., and Groves A.J., 2003, Exploration Licence 4846,
The Sisters, Annual Report to 29th May 2003, Endeavour Minerals Pty
Ltd., RIN
Willis, I.L., Brown, R.E., Stroud, W.J., Stevens, B.P.J., 1983,
The Early Proterozoic Willyama Supergroup: stratigraphic
subdivision and interpretation of high to low-grade metamorphic
rocks in the Broken Hill Block, New South Wales., Geological
Society of Australia Journal, 30(2), p195-2
This information is provided by RNS, the news service of the
London Stock Exchange. RNS is approved by the Financial Conduct
Authority to act as a Primary Information Provider in the United
Kingdom. Terms and conditions relating to the use and distribution
of this information may apply. For further information, please
contact rns@lseg.com or visit www.rns.com.
RNS may use your IP address to confirm compliance with the terms
and conditions, to analyse how you engage with the information
contained in this communication, and to share such analysis on an
anonymised basis with others as part of our commercial services.
For further information about how RNS and the London Stock Exchange
use the personal data you provide us, please see our Privacy
Policy.
END
DRLFFFELFTIDFIV
(END) Dow Jones Newswires
February 28, 2023 02:00 ET (07:00 GMT)
Castillo Copper (LSE:CCZ)
Historical Stock Chart
From Jun 2024 to Jul 2024
Castillo Copper (LSE:CCZ)
Historical Stock Chart
From Jul 2023 to Jul 2024